Polymer Property : Tensile Strength, Ultimate = 89.6 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	89.6 MPa	13000 psi	ASTM D638
Nylene® Vexel™ B12GF15 , 15% Glass Reinforced PBT Description: Vexel™ B12GF15 is a 15% glass fiber reinforced, general purpose PBT. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeri..
Tensile Strength, Ultimate	89.6 MPa	13000 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Lubri-Tech™ PK-5GP/7T Polyetheretherketone (PEEK), PTFE Lubricated (discontinued **) Description/Features:Graphite LubricatedPTFE LubricatedInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate	89.6 MPa	13000 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® AS-13CF/000 Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced (discontinued **) Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate	89.6 MPa	13000 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® AS-20CF/000 Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced (discontinued **) Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate	89.6 MPa	13000 psi
CE Phenolic Laminate Cotton based phenolic provides more mechanical strength than paper grades and has a finer surface with better machinability. This material is used for gears, pinions, bearings, bushings, and many s..
Tensile Strength, Ultimate	89.6 MPa @Temperature 482 Â°C	13000 psi @Temperature 900 Â°F	Monel butt joint
Lucas-Milhaupt EASY FLO Silver Based Cadmium-Bearing Filler Metal Applications: Easy-Flo is very versatile and can be used successfully on nearly all nickel, iron and copper base alloys. In certain instances, special fluxes, may be required to obtain good wettin..
Tensile Strength, Ultimate	89.6 MPa	13000 psi	ASTM D638
Adell ER-36 Homopolymer Polypropylene, 30% Glass Reinforced Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate	89.6 MPa	13000 psi	ASTM D638
Applied Composites 8007 Polyester SMC Industry Application: ConstructionProduct Application: Water TreatmentDistinct Features: Pigmentable, Low Water Absorption, Weathering Resistant, Good Corrosion Resistance in Waste Water Environment..
Tensile Strength, Ultimate	89.6 - 125 MPa	13000 - 18100 psi	Average value: 100 MPa Grade Count:8
Overview of materials for Polyphthalamide (PPA), 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are ..
Tensile Strength, Ultimate	89.6 MPa	13000 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Lubri-Tech™ RA-15GF/13T Polyethersulfone, Glass Filled, PTFE Lubricated (discontinued **) Description/Features:Glass Fiber ReinforcedPTFE LubricatedUL 94 V0UL 94 (CTI Testing)PolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate	89.6 MPa	13000 psi	ASTM D638
Adell ER-16 Homopolymer Polypropylene, 30% Glass Reinforced Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate	89.6 MPa	13000 psi	ASTM D638
Adell ER-17 Homopolymer Polypropylene, 30% Glass Reinforced Data provided by Adell Plastics, Inc.