Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 85.0 MPa @Temperature 60.0 °C |
12300 psi @Temperature 140 °F |
ISO 527 |
LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5 mm/min |
Polimeri Europa KOBLEND PCA PD 935 G4 PC+ABS, 20% Glass Fiber
(discontinued **) Symbol according to ISO 1043/1/2: PC+ABS (GF) Injection moulding grade, reinforced with 20% glass fibres, high stiffness, very good dimensional stability. Main application fields: structural non a.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ISO 527 |
LATI LATAN 13 K/30 30% Carbon Fiber Reinforced Polyoxymethylene Copolymer (POM)
(Unverified Data**) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
Tensile Strength, Ultimate | 85.0 - 237 MPa | 12300 - 34400 psi | Average value: 166 MPa Grade Count:185 |
Overview of materials for Nylon 6, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Tensile Strength, Ultimate | 85.0 MPa @Temperature 22.0 °C |
12300 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 0430 Unsaturated Polyester UP SMC 0430 is a low emission Class-A SMC for on-line painted exterior body applications on passenger cars. These compounds mould to parts with excellent surface quality for on-line painted body panel.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
Styrolution Terblend® N NG-06 30% Glass Filled ABS/PA6 (Conditioned) Terblend N NG-06 is a 30% glass fiber reinforced ABS/PA6 blend with extra high rigidity and dimensional stability.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ISO 527 |
Wellman Wellamid® GFT13-66 XE-N 13% Impact Modified Glass Reinforced Nylon 66/6, Lubricated & Heat Stabilized Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equ.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ISO 527 |
Wellman Wellamid® MR409 22H-N 40% Mineral Reinforced Nylon 66, Heat Stabilized Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM D638 |
Toyobo T-422-02R Nylon, Mineral-Reinforced Key Feature: High heat distortion and good toughness, high flowInformation provided by Toyobo Co., Ltd |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | dry; ISO 527-1/-2 |
DSM Akulon® K222-KGV5 25% Glass Reinforced, Flame Retardant (Halogen free), Heat Stabilized |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | dry; ISO 527-1/-2 |
DSM Akulon® K224-PG2 PA6-I-GF8 8% Glass Reinforced, Impact Modified |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | cond; ISO 527-1/-2 |
DSM Akulon® XG-FKGS6 PA6-GF30 FR 30% Glass Reinforced, Flame Retardant, Halogen free |
|||
Tensile Strength, Ultimate | 85.0 MPa @Temperature 160 °C |
12300 psi @Temperature 320 °F |
ISO 527-1/-2 |
DSM Stanyl® OCD2100 BK27021 PA46-GF40 40% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | Diametral tensile strength |
3M Filtek™ Z250 Universal Restorative Dental Composite 3M™ Filtek™ Z250 universal restorative is an esthetic, light cured, radiopaque composite specifically designed for use in anterior or posterior direct or indirect restorations. Bonding to tooth s.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4300 G2 BK5110 10% Glass Filled PBT Ultradur B 4300 G2 BK5110 is a pigmented black, easy flowing injection molding PBT with 10% glass fiber reinforcement for rigid, tough, and dimensionally stable parts. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4300 G2 LS High Speed BK15045 10% Glass Filled PBT |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8260 40% Mineral Filled PA6 (Dry) Ultramid 8260 is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Dry) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5 mm/min |
Arkema Group Rilsan® AZM 23 T6LD Nylon 12, 23% Glass Fiber Filled (Dry) Designation ISO 1874-PA12,MHLR,16-050,GF23Rigid grade with glass fiber filler (23%) for injection molding. Available colors: black and natural. Reinforced light and heat stabilizing agent. Mold-rele.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ATSM D638 |
Ashley Polymers Ashlene® 830SMS Nylon 6, MoS2 Filled Basic Nylon 6, medium viscosity, lubricated with Molybdenum Disulfide.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultramid® A3EG3 15% Glass Filled PA66 (Conditioned) Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
BASF Ultramid® B3M6 30% Mineral Filled PA6 (Dry) Ultramid B3M6 is a 30% mineral reinforced injection molding PA6 grade for industrial items requiring high impact strength and very high dimensional stability, excellent laser markability. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM D638 |
A. Schulman ComAlloy Comtuf® 413 Glass Reinforced, Polycarbonate/Polyester Alloy, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 637 Nylon 6/6, Glass/Mineral Reinforced, Flow Enhanced, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM data at 5 mm/min. |
BASF Capron® 8260 40% Mineral-Filled Nylon 6 (Dry)
(discontinued **) Capron 8260 is a 40% mineral reinforced polyamide 6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability includi.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM data at 5 mm/min. |
BASF Capron® 8333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron 8333G is a 33% glass reinforced nylon 6 modified compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness, and excel.. |
|||
Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ASTM D638 |
Chevron Phillips Ryton® PR09-60 Polyphenylene Sulfide Compound, Annealed 2 hours at 200°C
(discontinued **)&l Polyphenylene Sulfide CompoundRyton® PR09-60 Annealed 2 hours at 200°C is pelletized unfilled high molecular weight polyphenylene sulfide resin suitable for extrusion or injection molding.Comments.. |
|||
Tensile Strength, Ultimate | 85.0 MPa @Temperature 60.0 °C |
12300 psi @Temperature 140 °F |
ISO 527 |
LATI LARIL 13 G/30-V1 30% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |