Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
PSM Industries Pacific Sintered Metals Infiltrated High Carbon Steel FX-232-T(HT) Powdered Metal Good strength, shock resistance and hardenability, Moderate tolerance control Equivalent MPIF Specification: FX-1008-110HTInformation Provided by Pacific Sintered Metals, a division of PSM Industri.. |
|||
Tensile Strength, Ultimate | >= 827 MPa | >= 120000 psi | |
PSM Industries PolyAlloys WNF-3515 Tungsten Heavy Alloy Mil. T-21014 Class 3, SAE-AMS-T-21014 Class 3, ASTM-B-777-87 Class 3Information Provided by PolyAlloys, a division of PSM Industries |
|||
Tensile Strength, Ultimate | >= 827 MPa | >= 120000 psi | |
PSM Industries PolyAlloys WNF-7129 Tungsten Heavy Alloy Mil. T-21014 Class 1, SAE-AMS-T-21014 Class 1, AMS 7725 B, ASTM-B-777-87 Class 1Information Provided by PolyAlloys, a division of PSM Industries |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
Hogen Diemitechâ„¢ Tungsten-Based Metal Diemitech is a new tungsten-based material used for high temperature tooling, die casting, extrusion dies, hot upsetting, and electro brazing. It has a higher tungsten content than similar available.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
Hogen HM1100 Tungsten-Based Metal Mil Spec T-21014D Class 1; ASTM B-777-99 Class 1; SAE Aero Material Spec (AMS) 7725C; AMS T-21014 Class 1. Slightly Magnetic.Manufactured by powder metallurgy methods. The tungsten base offers hig.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
Hogen HM3050 Tungsten-Based Metal Mil Spec T-21014D Class 3; ASTM B-777-99 Class 3; AMS T-21014 Class 3. Slightly Magnetic.Manufactured by powder metallurgy methods. The tungsten base offers high thermal conductivity and a low CTE.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
FloMet 17-4 PH Stainless Steel, As Sintered FloMet provides precision miniature components through metal injection molding (MIM). Metal powders are mixed with thermoplastic binders to form a homogeneous mixture, with approximately 60% volume.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
Mi-Tech Metals Diemitechâ„¢ Tungsten-Based Metal Diemitech is a new tungsten-based material used for high temperature tooling, die casting, extrusion dies, hot upsetting, and electro brazing. It has a higher tungsten content than similar available.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
Mi-Tech Metals HD17D Tungsten-Based Metal Mil Spec T-21014D Class 1; ASTM B-777-99 Class 1; ASTM B-777-07 Class 1; SAE Aero Material Spec (AMS) 7725C; AMS T-21014 Class 1. Slightly Magnetic.Manufactured by powder metallurgy methods. The t.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
Mi-Tech Metals HD18D Tungsten-Based Metal Mil Spec T-21014D Class 3; ASTM B-777-99 Class 3; ASTM B-777-07 Class 3; AMS T-21014 Class 3. Slightly Magnetic.Manufactured by powder metallurgy methods. The tungsten base offers high thermal con.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | 621°C Temper Temperature |
Latrobe Lescalloy® 16NCD13 VAC-ARC High Strength Alloy Steel 16NCD13 VAC-ARC is a premium quality low alloy, carburizing casehardenable vacuum arc remelted steel which takes its name from the French industry designation. In the carburized condition, its high .. |
|||
Tensile Strength, Ultimate | 827 MPa @Temperature 427 °C |
120000 psi @Temperature 801 °F |
|
Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
Special Metals Electroformed Nickel, 6 Micron (0.24 mil) Foil, As-Electroformed Data provided by the manufacturer, Special Metals. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | Annealed |
Universal Wire Works 5Al-2.5Sn (AMS 4953) Titanium Alloy Filler Metal Universal Ti 5Al-2.5Sn titanium alloy is easily joined with the gas tungsten arc, gas metal arc or resistance welding processes. 100% joint efficiency can be obtained provided proper shielding proce.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
CMW® ELKON 100W Pure Tungsten Tungsten, also called Wolfram, occurs as an impure tungsten oxide in wolframite and sche ores. It is chemically extracted, refined to an oxide of high purity and reduced to tungsten powder in hydrog.. |
|||
Tensile Strength, Ultimate | >= 827 MPa | >= 120000 psi | Mid-radius |
Dura-Bar 120-90-02 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | cold worked |
CMW® ELKONIUM 301 platinum based alloy Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | cold worked |
CMW® ELKONIUM 306 platinum based alloy Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
CMW® THERMKON® 68 Tungsten Copper parts For matching CTE of semiconductor substrates while allowing high thermal transfer.Information provided by CMW Inc. |
|||
Tensile Strength, Ultimate | 827 MPa @Temperature -129 °C |
120000 psi @Temperature -200 °F |
Longitudinal |
Carpenter 20Cb-3® Stainless Steel Data provided by Carpenter Technology Corporation.20Cb-3® is an austenitic stainless steel possessing excellent resistance to hot sulfuric acid and many other aggressive environments which would re.. |
|||
Tensile Strength, Ultimate | 827 MPa @Thickness 50.8 mm |
120000 psi @Thickness 2.00 in |
Typical for Plate, Annealed |
AK Steel NITRONIC® 30 Austenitic Stainless Steel AK Steel NITRONIC 30 Stainless Steel offers significantly higher strength than Type 304 and potential for applications requiring good resistance to aqueous and atmospheric corrosion resistance combi.. |
|||
Tensile Strength, Ultimate | 827 - 965 MPa | 120000 - 140000 psi | |
Ametek AM 388™ Alloy (UNS C72650) TM06 Information supplied by Ametek Specialty Metal Products Division.Copper base Spinodal alloy with high conductivity and high strength. Outstanding performance for contacts in connectors, sockets and.. |
|||
Tensile Strength, Ultimate | 827 - 965 MPa | 120000 - 140000 psi | |
Ametek AM 388™ Alloy (UNS C72650) TX00 Information supplied by Ametek Specialty Metal Products Division.Copper base Spinodal alloy with high conductivity and high strength. Outstanding performance for contacts in connectors, sockets and.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
Carpenter Gall-Tough PLUS™ Stainless, Annealed, 10% Cold Work Data provided by Carpenter Technology Corporation.Annealed 1150°C, water quenched, and cold drawn.Threshold Galling Stress 48 MPa. The avg. total volume loss on the wear test is 10.6 mm³ at 100 r.. |
|||
Tensile Strength, Ultimate | >= 827 MPa | >= 120000 psi | For flat products (<4" thickness) and seamless tube and pipe |
ATI Allegheny Ludlum AL Altemp® 625 Nickel-Base Superalloy, UNS N06625 Allegheny Ludlum Altemp 625 alloy is an austenitic nickel-base superalloy possessing excellent resistance to oxidation and corrosion over a broad range of corrosive conditions, including jet engine .. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | Solution Annealed |
ATI Allegheny Ludlum Altemp® 263 Nickel-Based alloy Characteristics: high strength up to 1500°F, oxidation resistance up to 2000°FInformation provided by Allegheny Ludlum |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | Beta Quenched |
ATI Wah Chang Tiadyne™ 3510 Capable of being surface hardened to depths that produce very high wear resistance. Produced by traditional metallurgical processing, not special treatments.Information provided by ATI Wah Chang |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
Carpenter Hiperco® 50 Fe-Co-V Soft Magnetic Alloy, 0.15 mm Strip Heat Treated 760°C Hiperco® alloy 50 is an iron-cobalt-vanadium soft magnetic alloy which exhibits high magnetic saturation (24 kilogauss), high D.C. maximum permeability, low D.C. coercive force, and low A.C. core l.. |
|||
Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
Special Metals INCOLOY® 27-7MO Super-Austenitic Stainless Steel INCOLOY® alloy 27-7MO (UNS S31277; EP 1,263,999 B1) is an advanced 7% molybdenum super-austenitic stainless steel offering corrosion resistance in most environments superior to 6% molybdenum super-.. |