Polymer Property : Tensile Strength, Ultimate = 770 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	770 - 780 MPa	112000 - 113000 psi
Kennametal Stellite Denertiaâ„¢ C14 Cobalt Chromium Dental Alloy Denertiaâ„¢ C14 is a cobalt chromium base-metal casting alloy for the manufacture of removable partial dentures and bridgework. It conforms to the following International Standards: EN 1641 Â§..
Tensile Strength, Ultimate	770 - 940 MPa	112000 - 136000 psi
Industeel SUPRALSIMÂ® 690 HLE Steel for Welded and Weight-Saving Structures Description: SUPRALSIMÂ® 690 is general steel plate for structure enables to make weight savings thanks to a minimum yield strength of 690 N/mmÂ². Thanks to its exceptional purity rate (very low..
Tensile Strength, Ultimate	>= 770 MPa	>= 112000 psi
Industeel URANUSÂ® 52N+ 25 Cr Super Duplex Stainless Steel with PREN = 40 Description: URANUSÂ® 52N+ (UR 52N+) is a super duplex stainless steel with 25% Cr and a PREN value higher than 40. The minimum guaranteed yield strength is 550 MPa which allows the designer to re..
Tensile Strength, Ultimate	770 - 780 MPa	112000 - 113000 psi
Kennametal Stellite Denertiaâ„¢ C4 Cobalt Chromium Dental Alloy Denertiaâ„¢ C4 is a cobalt chromium base-metal casting alloy for the manufacture of removable partial dentures and bridgework.It conforms to the following International Standards: EN 1641 Â§4...
Tensile Strength, Ultimate	>= 770 MPa	>= 112000 psi
Industeel URANUSÂ® 47N+ 25 Cr Super Duplex Stainless Steel with PREN = 40 Description: CLI - SAF 2507Â® is a 25.07 super duplex stainless steel with 25% Cr and a PREN value higher than 40. The minimum guaranteed yield strength is 550 MPa which allows the designer to red..
Tensile Strength, Ultimate	770 MPa @Temperature 540 Â°C	112000 psi @Temperature 1000 Â°F
Haynes 25 alloy, cold rolled and 1205Â°C (2200Â°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	770 MPa @Temperature 540 Â°C	112000 psi @Temperature 1000 Â°F
Haynes 625 alloy, cold rolled and 1050Â°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Ultimate	770 MPa	112000 psi
Wieland 1914 Wilaform Gold Nickel and palladium-free white gold alloy with beautiful white color.Applications: casting, laminar decoration, pipes, tubingDental
Tensile Strength, Ultimate	770 - 870 MPa	112000 - 126000 psi
CLAL-MSX NICLAFOR® 1000 TF Quenched/Precipitation Heat Treated, Drawn Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Ultimate	770 MPa	112000 psi
Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..