Polymer Property : Tensile Strength, Ultimate = 745 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	745 MPa	108000 psi
Kennametal Stellite StelliteÂ® 31 PM cast Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we..
Tensile Strength, Ultimate	745 MPa @Temperature 760 Â°C	108000 psi @Temperature 1400 Â°F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370Â°C (700Â°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	745 MPa @Temperature 650 Â°C	108000 psi @Temperature 1200 Â°F
Haynes 25 alloy, cold rolled and 1205Â°C (2200Â°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	745 MPa	108000 psi
Haynes 556Â® alloy, bar, after 8000 hours at 870Â°C (1600Â°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	745 MPa @Temperature 425 Â°C	108000 psi @Temperature 797 Â°F
Haynes HastelloyÂ® B-3Â® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOYÂ® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Tensile Strength, Ultimate	745 MPa	108000 psi
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Forged Disc, Solution Treated Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, Solution Treated samples. Density and magnetic permeability are typical of ..
Tensile Strength, Ultimate	745 MPa	108000 psi
Wieland 1910 Wilaform Gold Nickel and palladium-free white gold alloy with beautiful white color.Applications: casting, laminar decoration, pipes, tubingDental
Tensile Strength, Ultimate	745 - 827 MPa	108000 - 120000 psi
Eagle Brass 770 Nickel Silver 18%, Spring 770 has good cold forming properties, is tarnish resistant and has very good spring properties. 770 does not become subject to embrittlement at lower temperature and it has excellent corrosion resi..
Tensile Strength, Ultimate	745 MPa	108000 psi	0% cold reduction
ATI Allegheny Ludlum AL 2003™ Duplex Stainless Steel Characteristics: superior stress corrosion cracking resistance to Types 316 and 317, yield strength double that of conventional austenitic stainless steel, good corrosion resistance, good chloride s..
Tensile Strength, Ultimate	745 MPa	108000 psi
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 305, 20% Cold Rolled (UNS S30500) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to ..
Tensile Strength, Ultimate	745 MPa @Thickness 3.20 mm	108000 psi @Thickness 0.126 in
Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is..