Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM data at 5 mm/min. |
BASF Capron® GR15 HS 15% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron GR15 HS is a heat stabilized 15% glass reinforced polyamide 6 injection molding compound possessing a balance of engineering properties combined with excellent processability and surface aest.. |
|||
Tensile Strength, Ultimate | 70.0 - 269 MPa | 10200 - 39000 psi | Average value: 189 MPa Grade Count:23 |
Overview of materials for Polyarylamide, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyarylamide, Glass Fiber Filled". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Ultimate | 70.0 - 165 MPa @Temperature 60.0 - 150 °C |
10200 - 23900 psi @Temperature 140 - 302 °F |
Average value: 113 MPa Grade Count:1 |
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Tensile Strength, Ultimate | 70.0 - 80.0 MPa @Time 1.80e+7 - 7.20e+7 sec |
10200 - 11600 psi @Time 5000 - 20000 hour |
Average value: 66.6 MPa Grade Count:2 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Tensile Strength, Ultimate | 70.0 - 155 MPa @Temperature 60.0 - 150 °C |
10200 - 22500 psi @Temperature 140 - 302 °F |
Average value: 61.4 MPa Grade Count:2 |
Overview of materials for Nylon 610 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610". Each property range of values reported is minimum and maximum values of appropriate MatWeb e.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
Ineos ABS Triax® 1315 GF ABS + Polyamide Blend (Conditioned) Key Features:Contains FillerSuitable processing methods:Injection molding |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
ICE Steatite L-5 Data provided by the manufacturer, International Ceramic Engineering. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
Lucite International Perspexâ„¢ XT Acrylic Extruded Sheet 0X00 PERSPEX extruded sheet has a lower molecular weight making it easy to vacuum form and the extrusion process gives excellent thickness tolerance and is economical for long production runs.Information.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
Haysite HCR-196 Corrosion Resistant Vinyl Ester/Glass Sheet A fiber glass reinforced thermoset sheet using DEREKANE® 470 vinylester in the resin matrix. Standard color is grey. Additional data covering resistance to specific chemicals is available upon re.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | Safety factor of 10-20X is necessary in practice |
Saint-Gobain Vitreosil® Clear Fused Quartz Tubing Electrically fused quartz is recognized for its combination of purity, chemical inertness, physical stability, thermal shock resistance, high electrical resistivity, and high operating temperatures... |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ISO 527 |
Sumitomo Bakelite North America RX® 660 Fiberglass Reinforced Phenolic Novolac RX 660 is a fiberglass reinforced phenolic molding compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type MFH.Information supplied by Sumitom.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ISO 527 |
Wellman Wellamid® 22LHI3 XE-N Impact Modified Nylon 66, Lubricated & Heat Stabilized Typical Applications: Automotive fasteners, living hinge, head lamp adjustment devices, ink pen components, wire separators, hardware components, window installation clips, safety equipment.Data pro.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ISO 527 |
Wellman Wellamid® GS40-60 42LH-N 40% Glass Sphere Filled Nylon 6, Lubricated & Heat Stabilized Typical Applications: Potentiometer liners, electrical coil forms, automotive window lift and power door lock switch bodies, gears, thick wall section moldings, emission control valves.Data provided.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D882 |
DuPont Selar® PA 2072 Nylon Barrier Resin Selar® PA 2072 is an amorphous nylon (polyamide) resin which is specially designed for blending with ethylene vinyl alcohol (EVOH) copolymers. Selar® PA 2072 can be tumble-blended with most grades.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
Covestro Makrolon® 8035 Polycarbonate High viscosity extrusion and injection molding grade with 30% short glass fibers and easy mold release, low anisotropy, for stiff moldings requiring good dimensional stability.Information provided b.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | cond; ISO 527-1/-2 |
DSM Novamid® 1013GH15 1 NA/BK37 PA6-GF15 15% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | cond; ISO 527-1/-2 |
DSM Akulon® K224-G3-FC NA99001 PA6-GF15 15% Glass Reinforced |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
BASF Procom® GC20H 250 Polypropylene Uses: car and truck fans and shrouds, car rear light housings, car radiator expansion tanks, car grills, domestic appliance components (e.g. washing machine tanks, impellers housings, etc.), textile.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | 5mm/min; ISO 527 |
BASF Ultramid® NFX-0102 NF2004 30% Glass Filled PA66 (Dry) Ultramid NFX-0102 NF2004 is a heat stabilized, 30% glass bead PA66 injection molding grade. It is especially formulated for low warp, increased stiffness and excellent dimensional stability. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 112 Polypropylene, Glass Reinforced, Chemically Coupled, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ATSM D638 |
Ashley Polymers Ashlene® 851 Nylon 6, High Viscosity High viscosity for blown film, tubing, rods and shapes and blow molding. Has highest puncture resistance and clarity. FDA and NSF approved.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 132 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.45% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 70.0 - 255 MPa | 10200 - 37000 psi | Average value: 166 MPa Grade Count:88 |
Overview of materials for Nylon 46, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Ultimate | 70.0 MPa @Temperature 704 °C |
10200 psi @Temperature 1300 °F |
|
AK Steel 439 ULTRA FORM® Stainless Steel AK Steel 439 ULTRA FORM™ was developed for applications requiring oxidation and corrosion resistance superior to Type 409 as well as superior formability to AK Steel 439 Stainless Steel. As a resul.. |
|||
Tensile Strength, Ultimate | 70.0 - 95.0 MPa @Temperature 60.0 - 150 °C |
10200 - 13800 psi @Temperature 140 - 302 °F |
Average value: 82.5 MPa Grade Count:1 |
Overview of materials for Polyethersulfone (PES), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% a.. |
|||
Tensile Strength, Ultimate | 70.0 - 175 MPa | 10200 - 25400 psi | Average value: 122 MPa Grade Count:71 |
Overview of materials for PBT + PET Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "PBT + PET Blend, Glass Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 663 Nylon 6, Glass Bead Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass Bead Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 70.0 - 100 MPa @Temperature -40.0 - -40.0 °C |
10200 - 14500 psi @Temperature -40.0 - -40.0 °F |
Average value: 85.0 MPa Grade Count:4 |
Overview of materials for Nylon 6, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Impact Grade". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
Solvay Specialty Polymers Ixef® 2010/X914 Polyarylamide, 40% Filler, at Equilibrium (65% RH)
(discontinued ** The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay A.. |
|||
Tensile Strength, Ultimate | 70.0 - 165 MPa | 10200 - 24000 psi | Average value: 123 MPa Grade Count:38 |
Overview of materials for Polybutylene Terephthalate (PBT), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Carbon Fiber Filled". Each property range of values reported is minimu.. |