Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
PTS Trimid® N66-S100L High Impact Nylon 6/6 Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Eastman Tenite Butyrate 438E0V16304 Clear, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 4%. Weight loss on heating = 0.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr.. |
|||
Tensile Strength, Ultimate | 51.0 - 69.0 MPa | 7400 - 10000 psi | Average value: 58.0 MPa Grade Count:10 |
Overview of materials for Phenolic, Resole, Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Resole, Wood Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | DIN 53455; ASTM D638 |
Kolon Kopa® KN161 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | |
Kuraray HYBRAR® PS3 Thermoplastic Rubber-Polystyrene Blend Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
LyondellBasell Higlass SB224-2 Polypropylene Copolymer, 20% Glass Fiber Key Features: conventional melt flow, medium modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, high impact strength, moderate rigidity, good processabilityApplications: of.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 1501 Polyester, Briquette, Transfer Molded PLENCO 01501 is a general purpose, mineral filled granular polyester molding compound, offering excellent arc and track resistance properties, low post shrinkage, and improved mechanical strength va.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 2000 Phenolic, Granular, Compression Molded PLENCO 02000 is a versatile general purpose, organic filled phenolic molding compound, offering optimum cure characteristics and an excellent balance of molding properties. UL recognized under compo.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 2571 Phenolic, Granular, Transfer Molded PLENCO 02571 is a general purpose, organic filled phenolic molding compound offering optimum cure characteristics while maintaining excellent mechanical and electrical properties. UL recognized unde.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 3303 Phenolic, Granular, Compression Molded Plenco 03303 is a renumber of Plaslok 5303. Plenco 03303 is a two-stage, mineral and flock-filled phenolic molding compound offering excellent electrical insulating properties. It can be processed b.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 3356 Phenolic, Granular, Injection Molded PLENCO 03356 is a mineral filled phenolic molding compound offering excellent arc resistance, comparative tracking, and flame resistant properties. UL recognized under component file E40654. 03356 i.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 6990 Phenolic, Briquette, Compression Molded PLENCO 06990 is a glass and mineral filled novolac phenolic molding compound. UL recognized under component file E40654.Information supplied by Plenco. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Toyobo A1071D Thermoplastic Polyurethane Elastomer, Injection Grade Polybutyleneadipate type, the most general purpose type of Toyobo Polyurethane; features excellent cost-performance. Various grades of Toyobo polyurethane TPEs are used in auto parts, hoses, tubes,.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ISO 37 |
Lubrizol ESTANE® 58134 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | |
Elastomer Engineering E60D Polyurethane A polyester-based urethane with particularly high load-bearing characteristics. Information provided by Elastomer Engineering Inc (EEI) |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ISO 527-1, 2 |
Polyplastics Duranex® 652SA Polybutylene Terephthalate (PBT), Low density, Low wear, Mineral filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | DIN 53 504 |
Dow BETAMATE™ 5103-2 Epoxy BETAMATE™ 5103-2 is a one component heat curing Epoxy paste adhesive. The material is readily pumped at ambient temperatures. It shows excellent adhesion to automotive steel, including coated ste.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Covestro Makroblend® EL 703 Polycarbonate + Polyester-based Blend, Impact Modified, Flame-Retardant, UV Stabilized Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboWeld 48-14/AboCure 48-14 Adhesive/Casting Resin Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboWeld 48-8/AboCure 48-8 Adhesive/Casting Resin Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | 0.5 x 0.125 in. specimen; 0.2 in/min; ASTM D638 |
Americas Styrenics STYRON™ 668 General Purpose Polystyrene Resin STYRON™ 668 is a general purpose polystyrene with medium flow and a balance of heat resistance and stiffness characteristics that make it suitable for applications such as CD jewel boxes. STYRON™.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ATSM D638 |
Ashley Polymers Ashlene® 733LD Nylon 6 A modified injection molding grade nylon for applications requiring flexibility.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ATSM D638 |
Ashley Polymers Ashlene® P254WO PPO A general purpose V-0 rated resin with high impact strength.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboCast 37-10/AboCure 37-10 Adhesive/Casting Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboCast 53-15/AboCure 53-15 Adhesive/Casting Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Adell ZS-30 Nylon/Olefin Alloy Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 51.0 - 240 MPa | 7400 - 34800 psi | Average value: 148 MPa Grade Count:161 |
Overview of materials for Polyetheretherketone, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Glass Fiber Filled". Each property range of values reported is minimum and maximum.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ISO 527B |
Ineos Nova 201 Crystal Polystyrene High Heat Extrusion Grade
(discontinued **) Excellent heat resistance, Superior melt strengthApplications: Foam insulation, Oriented polystyrene sheet (OPS), XPS food packaging, Sheet and profile extrusionProperties were determined on injecti.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | 5 mm/min; parallel to flow; ASTM D638 |
Asahi Kasei Tenac®-C EF750 Acetal Copolymer, Antistat
(discontinued **) Antistatic grade containing special carbon black.Applications: Parts requiring antistatic properties.This product is not a part of the standard product line dated 2003. |
|||
Tensile Strength, Ultimate | 51.0 MPa @Temperature 120 °C |
7400 psi @Temperature 248 °F |
ISO 527 |
LATI LARIL 13 G/30-V1 30% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |