Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 476 MPa | 69000 psi | |
Universal Wire Works 2319 (AMS 4191) Aluminum Alloy Filler Metal Alloy 2319 is used on applications requiring good strength at high temperatures (600°F) and many cryogenic and aircraft parts. Primarily used where weld joints are capable of being heat treated to .. |
|||
Tensile Strength, Ultimate | 476 - 565 MPa | 69000 - 82000 psi | |
Eagle Brass 18665 MSP1, Hard MSP-1 high performance copper alloy with magnesium has high conductivity (63% IACS), high strength and excellent thermal creep properties. Typical uses include terminals, connectors, relays, springs.. |
|||
Tensile Strength, Ultimate | 476 - 531 MPa | 69000 - 77000 psi | |
Eagle Brass 220 Commercial Bronze, Spring CDA 220 is known for having very good corrosion resistance, great cold workability and good hot workability for drawing, blanking, coining, stamping, piercing and punching. Typical uses include plum.. |
|||
Tensile Strength, Ultimate | 476 - 579 MPa | 69000 - 84000 psi | |
Eagle Brass 521 Phosphor Bronzes 8% C, 1/2 Hard Alloy C521 is a high tin alloy of the phosphor bronze family. The additional tin relative to the more commonly used C510 results in higher mechanical properties with a modest reduction in electrical.. |
|||
Tensile Strength, Ultimate | 476 - 545 MPa | 69000 - 79000 psi | |
Eagle Brass 735 Nickel Silver 18%, 3/4 Hard 735 is used for coinage, name plates, zippers, flatware, and fashion jewelry.Information provided by Eagle Brass Company |
|||
Tensile Strength, Ultimate | 476 - 600 MPa | 69000 - 87000 psi | |
Eagle Brass 770 Nickel Silver 18%, 1/4 Hard 770 has good cold forming properties, is tarnish resistant and has very good spring properties. 770 does not become subject to embrittlement at lower temperature and it has excellent corrosion resi.. |