Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 400 MPa | 58000 psi | |
Pacific Sintered Materials FCC-200-P High Carbon Copper Steel Powdered Metal High strength, good impact resistant material for mechanical components. Excellent hardenability. High performance material with high strength and wear resistance after heat treatment.Equivalent MPI.. |
|||
Tensile Strength, Ultimate | 400 MPa @Temperature 870 °C |
58000 psi @Temperature 1600 °F |
|
Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Ultimate | >= 400 MPa | >= 58000 psi | |
H.C. Starck WCu 75/25 Tungsten-Copper Composite Material Description of Product: Tungsten-copper composite materials are produced by copper infiltration of porous sintered tungsten. They are available with different copper contents (10 - 30 %). A therm.. |
|||
Tensile Strength, Ultimate | 400 MPa @Temperature 870 °C |
58000 psi @Temperature 1600 °F |
|
Haynes Hastelloy® alloy 188 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
Tensile Strength, Ultimate | 400 MPa @Temperature 300 °C |
58000 psi @Temperature 572 °F |
Annealed prior to test |
Special Metals NILO® Alloy K Controlled-Expansion Alloy Inflection point 450°C. A nickel-iron-cobalt controlled-expansion alloy containing 29% nickel. Its coefficient of expansion, which decreases with rising temperature to the inflection point, mat.. |
|||
Tensile Strength, Ultimate | 400 - 480 MPa | 58000 - 69600 psi | |
SSAB Tunnplat Docol® 400DP High-strength Steel High-strength SteelComments: Docol DP - Cold Rolled Steel - dual-phase steel. Property values are for cold-rolled steel; thicknesses 0.5 - 1.6 mm. Iron content is approximate - exact composition is.. |
|||
Tensile Strength, Ultimate | <= 400 MPa | <= 58000 psi | |
SSAB Tunnplat Domex® 200 Cold-forming Steel Cold-forming SteelCharacteristics: Domex® is specifically intended for deep-drawing operations. Due to its close tolerances and fine surfaces, hot-rolled Domex 200 can replace cold reduced deep-.. |
|||
Tensile Strength, Ultimate | 400 MPa | 58000 psi | |
Wieland 1403 Wilaform Gold Hard yellow gold alloy. Universally applicable in decoration production. Since it does not posses a very fine-grained structure it is used frequently for chainsApplications: casting, chains, lamin.. |
|||
Tensile Strength, Ultimate | 400 MPa | 58000 psi | |
Wieland 1001 Wilaform Gold Hard 333/standard yellow gold alloy. Particularly suited for strongly stressed parts.Applications: casting, laminar decoration, pipes, tubingDental |
|||
Tensile Strength, Ultimate | 400 - 496 MPa | 58000 - 72000 psi | |
Eagle Brass 706 Copper Nickel 10%, 1/2 Hard 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to.. |
|||
Tensile Strength, Ultimate | <= 400 MPa | <= 58000 psi | Rod |
CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. Its machineability is one of the best of all of the corrosion resistant alloys. The very good machineability of.. |
|||
Tensile Strength, Ultimate | <= 400 MPa | <= 58000 psi | |
CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Tensile Strength, Ultimate | 400 - 500 MPa | 58000 - 72500 psi | |
CLAL-MSX NICLAFOR® 1000 TB Quenched Drawn Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi.. |
|||
Tensile Strength, Ultimate | 400 - 470 MPa | 58000 - 68200 psi | |
CLAL-MSX SICLANIC S® TD4 Quenched Copper Alloy, 4/4 Hard SICLANIC S® is particularly recommended for the production of conductive contact blades. SICLANIC S® offers :electrical conductivity greatly superior to that of bronzes, brasses and nickel silver.. |
|||
Tensile Strength, Ultimate | 400 MPa | 58000 psi | cold worked |
CMW® ELKONIUM 217 Silver Cadmium Alloy The alloying of silver with cadmium produces materials with good arc extinction, good corrosion resistance and low contact resistance characteristics and provides them with good switching capability.. |
|||
Tensile Strength, Ultimate | 400 MPa | 58000 psi | annealed |
CMW® ELKONIUM 76 gold based alloy Pure gold has complete resistance to atmospheric tarnish and oxidation. It does not contribute to polymer formations like platinum and palladium alloys. Wrought gold metal is very soft and prone to .. |
|||
Tensile Strength, Ultimate | 400 - 460 MPa | 58000 - 66700 psi | |
ArcelorMittal IF 300 High strength IF steel, Cold rolled Available in the following: Extragal®/Galvannealed (HX300YD+Z/+ZF)Description: These steels were designed to provide an excellent combination of drawability and mechanical strength based on their .. |
|||
Tensile Strength, Ultimate | >= 400 MPa | >= 58000 psi | |
AK Steel ASTM A 1011, Grade 36 Type 2 Hot Rolled Carbon Steel, Structural Steel (SS) Type 2 for conversion to A36Information provided by AK Steel |
|||
Tensile Strength, Ultimate | 400 - 480 MPa | 58000 - 69600 psi | |
ArcelorMittal H 360 Solid solution steel, Cold rolled Available in the following: uncoated (HC300P) and electrogalvanized (HC300P+ZE) Description: Solid solution steels are designed to provide high strength while maintaining good drawability. These ste.. |