Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO D-6500 Multi-Flex® D 6500 is well suited for TPO extrusion applications and certain high value molded parts for the telecommunications industry.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
NCMT NanoPAC™ HG500 High Performance Polypropylene Nanocomposite Applications: Household Industry Electrical AppliancesInformation provided by Nano Composite Materials Technology Limited |
|||
Tensile Strength, Ultimate | 29.0 - 147 MPa | 4210 - 21300 psi | Average value: 70.3 MPa Grade Count:77 |
Overview of materials for Polybutylene Terephthalate (PBT), Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Flame Retardant". Each property range of values reported is minimum an.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Rotuba MS Cellulose Acetate Property values at 50% RH.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 29.0 - 51.0 MPa | 4210 - 7400 psi | Average value: 39.7 MPa Grade Count:14 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded". Each property range of values reported is m.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Ineos ABS Lustran® 266 Specialty, Transparent
(discontinued **) A clear injection molding grade of ABS. This transparent, general-purpose grade provides clarity and toughness with ease of processing. Used in housings, toys, lawn and garden applications, and va.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
North Wood Plastics PS with 40% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
Tensile Strength, Ultimate | 29.0 MPa @Temperature 90.0 °C |
4210 psi @Temperature 194 °F |
ISO 527 |
LATI LATILUB 73/13-01M Polyoxymethylene Base (POM), 1% Molybdenum Disulfide Self Lubricating Plastic
(Unv Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri.. |
|||
Tensile Strength, Ultimate | 29.0 - 138 MPa | 4210 - 20000 psi | Average value: 72.7 MPa Grade Count:55 |
Overview of materials for Polycarbonate, Stainless Steel Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Stainless Steel Fiber". Each property range of values reported is minimum and maximum val.. |
|||
Tensile Strength, Ultimate | 29.0 - 40.0 MPa | 4210 - 5800 psi | Average value: 34.4 MPa Grade Count:16 |
Overview of materials for High Density Polyethylene (HDPE), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Film Grade". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
DuPont™ Surlyn® 8527 Ionomer Resin, Sodium
(discontinued **) Surlyn® 8527 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
LyondellBasell Astryn 65F4-2 Polypropylene Homopolymer, 20% Talc Key Features: conventional melt flow, high modulus, mineral-filled polypropylene homopolymer, excellent impact and stiffness balance, good dimensional stability, excellent heat resistance, good colo.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Elastomer Engineering Elastamide 300 Elastomer Modified RIM Nylon 6 22% crystallinity. Information supplied by Elastomer Engineering. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4200 psi | |
Williams Advanced Alloys WS295 Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Total PPR 7525MZ Polypropylene, Injection Molding Grade Clarified random copolymer for injection moldingClarity - FINA 7525MZ exhibits superior clarity in molded parts.Impact - FINA 7525MZ produces molded parts with improved impact compared with parts mo.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4200 psi | ASTM D638 |
American Polymers API 505 Polystyrene API 505 is an intermediate grade of impact modified polystyrene. This material has exceptional moldability and colorability.Applications: API 505 is widely used in housewares, toys, containers, dis.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Eastman PROVISTA Copolymer PETG Copolyester Color, b* CIELAB, Illuminant D6500, 10° Observer is 0.61 per ASTM D 2244.Product Description: PROVISTA Copolymer is a resin specifically developed for extrusion into profiles where aesthetics like.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638/D412 |
Covestro Bayflex® XGT-140 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ISO 527 |
DSM Fibre Intermediates Nyrim® 3000 (Conditioned) Conditioned at 23°C and 50% Relative Humidity.Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is proc.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | Die C (35 min / 145°C); ASTM D412 |
Dow Buna® SB 1502 Cold polymerized Emulsion Styrene Butadiene Rubber (E-SBR) Buna® SB 1502 - Schkopau is manufactured by cold polymerization using mixed rosin acid / fatty acid soaps. A non-discoloring stabilizer is added during the production process. Buna® SB 1502 - Sc.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM Data |
Dow Retain® PS-4578 Polystyrene Data provided by Dow Chemical. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Adell EZ-14 Homopolymer Polypropylene, 20% Calcium Carbonate Filled Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4200 psi | after optimum cure |
Armstrong A-5/E Epoxy Adhesive Information provided by Ellsworth Adhesives. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Buckeye Polymers BP RPP 3019 TU Polypropylene, 30% Mineral Filled UV StabilizedThis Talc-filled product exhibits excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and mar resistan.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Devcon Wear Guard (High Load) Epoxy Abrasion-Resistant SystemComments: PuttyData provided by Ellsworth Adhesives. |
|||
Tensile Strength, Ultimate | 29.0 - 80.0 MPa @Temperature -40.0 - 120 °C |
4210 - 11600 psi @Temperature -40.0 - 248 °F |
Average value: 45.0 MPa Grade Count:4 |
Overview of materials for Nylon 6, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ISO 37 |
Lubrizol ESTANE® 58238 Ester Based Thermoplastic Polyurethane (European Grade) Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability in a flexible.. |
|||
Tensile Strength, Ultimate | 29.0 - 39.0 MPa | 4210 - 5660 psi | ISO 527 |
BASF Ecovio® C2203 F Blend Biodegradable Polyester Description: Ecovio® F Blend C2203 is our biodegradable film product containing renewable resources. It is basically a compound of our biodegradable copolyester Ecoflex® F Blend and polylactic aci.. |
|||
Tensile Strength, Ultimate | 29.0 - 153 MPa | 4210 - 22200 psi | Average value: 101 MPa Grade Count:42 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified". Each property range of values reported.. |