Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 23.4 MPa | 3390 psi | Measured on extruded film, ASTM D638 |
3M Dyneon™ THV™ 400 Fluorothermoplastic
(discontinued **) Data provided by the manufacturer, Dyneon LLC.This unique, melt-processable, tetrafluoroethylene, hexafluoropropylene, and vinylidene fluoride (THV) terpolymer provides a unique combination of perf.. |
|||
Tensile Strength, Ultimate | 23.4 MPa | 3400 psi | |
Sylvin Technologies 9604-85C Clear PVC for Injection Molding Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 23.4 MPa | 3400 psi | |
Williams Advanced Alloys WS304 Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
Tensile Strength, Ultimate | 23.4 MPa | 3390 psi | ASTM D638 |
DuPont™ Surlyn® 8660 Ionomer Resin, Sodium Surlyn® 8660 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu.. |
|||
Tensile Strength, Ultimate | 23.4 MPa | 3390 psi | Molded property |
Dow Primacor® 1410 Ethylene Acrylic Acid (EAA) Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical. |
|||
Tensile Strength, Ultimate | 23.4 MPa | 3390 psi | ASTM D638 |
Adell EZ-18 Homopolymer Polypropylene, 40% Calcium Carbonate Filled Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 23.4 - 33.1 MPa | 3390 - 4800 psi | Average value: 28.3 MPa Grade Count:13 |
Overview of materials for Polypropylene, Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Blow Molding Grade". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Ultimate | 23.4 MPa | 3390 psi | ASTM D638 |
Buckeye Polymers BP RPP 4010 TP Blk Reprocessed Polypropylene, 40% Mineral Filled Talc Filled BlackThis reprocessed product is successful in applications where cost is a major specification, yet physical characteristics require product performance. Industrial recycled resin comp.. |