Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO D-6403 Multi-Flex® D 6403 is a rubber modified polypropylene compound for automotive applications such as bumper-covers, step in pads, rubstrips, and airdams.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D638-95 |
Multibase Multi-Pro® 0710 C Brown Polypropylene Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D638 |
Multibase Multi-Pro® 1510 CNU White Polypropylene Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D638-95 |
Multibase Multi-Pro® 4013 CU Yellow 40% Filler Content Polypropylene Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 20.7 - 96.0 MPa | 3000 - 13900 psi | Average value: 65.0 MPa Grade Count:14 |
Overview of materials for Thermoplastic Polyurethane, Elastomer, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane, Elastomer, Glass Filled". Each property range of values reported is minimum .. |
|||
Tensile Strength, Ultimate | 20.7 - 331 MPa | 3000 - 48000 psi | Average value: 58.7 MPa Grade Count:190 |
Overview of materials for Nylon 66, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Impact Grade". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | 2 in/min.; ASTM D638 |
Ineos H00G-00 Polypropylene Homopolymer A polypropylene homopolymer produced by Ineos utilizing catalyst technology. This material meets the Food and Drug Administration requirements of 21CFR 177.1520. Homopolymer H00G-00 meets certain .. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | |
Sylvin Technologies 5748 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D882 |
Total PPR 8650 Polypropylene, Random Copolymer ATOFINA 8650 is a low melting, high ethylene random copolymer with improved color, optics and impact properties. The low melting point of ATOFINA 8650 makes it an excellent heat seal layer for orie.. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | |
Cytec EN-2532 (Conap) Potting and Encapsulation Adhesive Polyurethane Potting and Encapsulating SystemsConathane® EN-2500 series polyurethane potting and encapsulating systems from Cytek have varying degrees of worklife, viscosity and hardness for many s.. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | Molded property |
Dow Primacor® 1430 Ethylene Acrylic Acid (EAA) Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D412 |
Dow SPECTRIM™ 35-S Reaction Moldable Polymer SPECTRIM™ 35-S reaction moldable polymer is a two-component polyurethane system that incorporates advanced internal mold release (IMR) technology developed by the Dow Chemical Company.Information p.. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D412 |
Dow Tyrin® CM0136 Formulation FormulationTyrin® CPE Elastomer |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D412 |
Colorite Polymers CS1524SP Wire and Cable Insulation Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai.. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | |
Colorite Polymers 9012 Clear Injection Molding Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for injection molding of various components such as drip chambers, connectors, valves, etc. The vinyl c.. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | |
Dymax 3072 Solvent-Free Plastic Adhesive Solvent-Free Adhesives for Plastic Assembly in SecondsDymax® Light-Weld® and Ultra 3000 Series UV and UV/Visible Curing Adhesives for plastic assembly provide instant durable bonds to cure a wide .. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | |
Dymax 3073 Solvent-Free Plastic Adhesive Solvent-Free Adhesives for Plastic Assembly in SecondsDymax® Light-Weld® and Ultra 3000 Series UV and UV/Visible Curing Adhesives for plastic assembly provide instant durable bonds to cure a wide .. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | |
Dymax 602 Structural Adhesive Structural Adhesives for Rugged Bonding, Sealing, Tacking and Potting in SecondsMulti-Cure® 600 Series products are rapid setting adhesives that cure by UV light, activator or heat. These products .. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | |
Dymax 9-911 Strain Relief, Wire and Parts Tacking Adhesive High Performance Light-Curing Adhesives and Coatings for Electronic AssemblyDymax 9-911 Strain Relief, Wire and Parts Tacking AdhesiveRapid, high strength, designed for difficult substrates, resists.. |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D638 |
Arkema Group Solarkote® P-610 Acrylic PVC Capstock, clear, low glossInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D638 |
Arkema Group Solarkote® P-601 Acrylic PVC Capstock, white, high glossInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
DuPont Performance Polymers VTR 8600 (GF-S) Peroxide Cured Fluoroelastomer (FKM)
(discontinued **) FormulationVTR-8600 |
|||
Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D412-80 |
DuPont Performance Polymers Hypalon® 4085 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound
(disc Mineral filled compound with 100 parts Hypalon; 80 parts hard clay; 4 parts magnesia; 30 parts aromatic process oil; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont .. |
|||
Tensile Strength, Ultimate | 20.7 - 24.1 MPa | 3000 - 3500 psi | TM R050-36 |
Resinlab® EP1305LV Black Epoxy Casting Resin Resinlab™ EP1305LV Black is a black two-part epoxy casting resin designed to give good adhesion to metals and especially PVC. It has good wetting to most surfaces and is free flowing to penetrate c.. |
|||
Tensile Strength, Ultimate | 20.7 - 24.1 MPa | 3000 - 3500 psi | TM R050-36 |
Resinlab® EP1305LV Clear Epoxy Casting Resin Resinlab™ EP1305LV Clear is a black two-part epoxy casting resin designed to give good adhesion to metals and especially PVC. It has good wetting to most surfaces and is free flowing to penetrate c.. |