Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 18.5 MPa | 2680 psi | ASTM D412-80 |
DuPont Performance Polymers Hypalon® 45 Chlorosulfonated Polyethylene Rubber, Peroxide Cured Carbon Black Filled Compound Carbon black compound with 100 parts Hypalon; 40 parts carbon black; 20 parts magnesia; and 5.8 parts Varox® DBPH-50. Physical property data below (except mooney viscosity) are for vulcanizate. Ma.. |
|||
Tensile Strength, Ultimate | 18.5 MPa | 2680 psi | |
Freudenberg Simrit Simriz® 485 Universal FFKT Perfluoroelastomer Compound Perfluoro elastomers – or FFKM for short – have an ideal combination of characteristics, with their excellent chemical resistance, high level of temperature resistance, and high levels of .. |
|||
Tensile Strength, Ultimate | 18.5 MPa | 2680 psi | 35'/145°C; ASTM D412 |
SYNTHOS Kralex® 1712 Styrene Butadiene Rubber KRALEX® 1712 is a standard grade of oil extended styrene butadiene rubber. It is produced by a technology of cold emulsion polymerisation based on soaps of rosin and fatty acids and contains 23.5.. |
|||
Tensile Strength, Ultimate | 18.5 MPa | 2680 psi | 35'/145°C; ASTM D412 |
SYNTHOS Kralex® 1721 Styrene Butadiene Rubber KRALEX® 1721 is a standard grade of oil extended styrene butadiene rubber. It is produced by a technology of cold emulsion polymerisation based on soaps of rosin and fatty acids and contains 40% .. |
|||
Tensile Strength, Ultimate | 18.5 MPa | 2680 psi | 35'/145°C; ASTM D412 |
SYNTHOS Kralex® 1723 Styrene Butadiene Rubber KRALEX® 1723 is a Specific grade of oil extended styrene butadiene rubber. It is produced by a technology of cold emulsion polymerisation based on soaps of rosin and fatty acids and contains 23.5.. |
|||
Tensile Strength, Ultimate | 18.5 MPa | 2680 psi | 35'/145°C; ASTM D412 |
SYNTHOS Kralex® 1732 Styrene Butadiene Rubber KRALEX® 1732 is a Specific grade of oil extended styrene butadiene rubber. It is produced by a technology of cold emulsion polymerisation based on soaps of rosin and fatty acids and contains 32% .. |
|||
Tensile Strength, Ultimate | 18.5 MPa | 2680 psi | 35'/145°C; ASTM D412 |
SYNTHOS Kralex® 1739 Styrene Butadiene Rubber KRALEX® 1739 is a Specific grade of oil extended styrene butadiene rubber. It is produced by a technology of cold emulsion polymerisation based on soaps of rosin and fatty acids and contains 40% .. |
|||
Tensile Strength, Ultimate | 18.5 MPa | 2680 psi | 35'/145°C; ASTM D412 |
SYNTHOS Kralex® 1778 Styrene Butadiene Rubber KRALEX® 1778 is a Specific grade of oil extended styrene butadiene rubber. It is produced by a technology of cold emulsion polymerisation based on soaps of rosin and fatty acids and contains 23.5.. |