Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 177 - 200 MPa | 25600 - 29000 psi | Average value: 187 MPa Grade Count:5 |
Overview of materials for Polyetherimide (PEI), 40% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 40% Glass Fiber". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Tensile Strength, Ultimate | 177 MPa | 25700 psi | DIN 53455; ASTM D638 |
Kolon Kopa® KN133HB55 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Tensile Strength, Ultimate | 177 MPa | 25700 psi | ASTM D638 |
Solvay Specialty Polymers Amodel® AF-1145 V0 Polyphthalamide (PPA) Resin, 45% Glass Reinforced, at 50% RH
(di AMODEL AF-1145 V0 is a 45% glass reinforced, flame retarded polyphthalamide (PPA) which exhibits a high heat distortion temperature, high tensile strength and flexural modulus. The material is rela.. |
|||
Tensile Strength, Ultimate | 177 MPa | 25700 psi | 5mm/min; ISO 527 |
BASF Ultramid® B3WG6 BK00564 BGVW 30% Glass Filled PA6 (Dry) Ultramid B3WG6 BK00564 BGVW is a 30% glass fiber reinforced, pigmented black, heat stabilized injection molding PA6 grade. |