Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ASTM D638 |
Nylene® Vexel™ B12GF45 , 45% Glass Reinforced PBT Description: Vexel™ B12GF45 is a 45% glass fiber reinforced, general purpose PBT. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeri.. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ASTM D638 |
Nylene® Vexel™ B12GF45 SA , 45% Glass Reinforced PBT Description: Vexel™ B12GF45 SA is a 45% glass fiber reinforced PBT with improved surface aPolyphenylene Etherarance. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are.. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ISO value at 5mm/min. |
BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9333G is a 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface a.. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ISO value at 5mm/min. |
BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with.. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® PS-30CF/000 Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced
(discontinued **) Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ASTM D638 |
PolyOne Edgetek® ES-40GF/000 Polyethersulfone - 40% Glass Fiber Reinforced
(discontinued **) Data provided by PolyOne. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Stat-Tech™ PI-30GF/15SS Polyetherimide (PEI), Glass Filled
(discontinued **) Description/Features:Electrically ConductiveGlass Fiber ReinforcedStainless Steel Fiber FilledPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ASTM D638 |
Techmer ES Electrafil® J-50/CF/30 Polycarbonate, 30% Carbon Fiber Reinforced Carbon Fiber Reinforced |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ISO 527-1, 2 |
Polyplastics FR-PET® B3045FA Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose Information provided by PolyPlastics. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | |
Total PPH 3276 Polypropylene, Oriented Film Extrusion Grade Homopolymer film gradeLow Residuals – Fina 3276 utilizes the new Fina proprietary process technology to provide extremely low residuals for improved color stability and clarity.Slip/Antiblock .. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ASTM D638 |
Adell AT-37 Nylon 66, 35% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ATSM D638 |
Ashley Polymers Ashlene® P1440 Polycarbonate, 40% Glass Reinforced A 40% glass reinforced polycarbonate for maximum mechanical strength and thermal properties. P1443 with UV stabilizer.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 414 Polyester - PBT, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 517 Polycarbonate, Carbon Fiber Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ASTM D638 |
Adell AT-17 Nylon 66, 35% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ATSM D638 |
Ashley Polymers Ashlene® PBT 130, 50% Glass Reinforced A 50% glass reinforced PBT designed for maximum rigidity of engineered parts.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 656 Nylon 6/6, Carbon/Glass Fiber Reinforced, Flow Enhanced, UL Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ISO value at 5mm/min. |
BASF Capron® 8333G Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G is a 33% glass reinforced nylon 6 modified compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness, and excel.. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ISO value at 5mm/min. |
BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G HI is a 33% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance .. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 716 PPS, Carbon Fiber Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 152 MPa | 22000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Lubri-Tech™ PI-30GF/15T Polyetherimide (PEI), Glass Filled, PTFE Lubricated
(discontinued **) Description/Features:Glass Fiber ReinforcedPTFE LubricatedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation. |