Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 1500 MPa | 218000 psi | |
International Mold Steel Premium H13 Hot Work Die and Mold Steel Description: International Mold Steel's Premium H-13 is a chromium-based, hot work die and plastic mold steel designed for increased production rates and longer tool life. It meets the restricti.. |
|||
Tensile Strength, Ultimate | 1500 MPa | 218000 psi | |
Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Tensile Strength, Ultimate | 1500 MPa @Temperature -196 °C |
218000 psi @Temperature -320 °F |
|
Universal Wire Works 6Al-4V (ELI) (AMS 4956) Titanium Alloy Filler Metal Universal titanium alloy 6Al-4V (ELI) is similar to type 6Al-4V in chemical analysis with the exception of Extra Low Interstitial gases (ELI). By controlling these contaminating gases the fracture t.. |
|||
Tensile Strength, Ultimate | 1500 MPa | 218000 psi | Perpendicular to Thickness |
Zircar Ceramics Alumina Mat A layered, low density flexible mat made of 100% polycrystalline alumina fiber (non-RCF) designed for use to temperatures as high as 1650°C (3002°F). Shot free low density mat used as fill between.. |
|||
Tensile Strength, Ultimate | 1500 MPa | 218000 psi | at HRC 45 |
Bohler-Uddeholm UDDEHOLM MIRRAX ESR Plastic Mold Steel Uddeholm Mirrax ESR is specially developed and adapted for larger molds that require corrosion resistance and/or high surface finish.It is characterized by:High hardenability for consistent properti.. |
|||
Tensile Strength, Ultimate | 1500 MPa | 218000 psi | after hot stamping |
ArcelorMittal Usibor® 1500 Ultra high strength steel, Cold Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to .. |
|||
Tensile Strength, Ultimate | 1500 MPa | 218000 psi | after hot stamping |
ArcelorMittal Usibor® 1500 Ultra high strength steel, Hot Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to .. |
|||
Tensile Strength, Ultimate | 1500 MPa | 218000 psi | after hot stamping |
ArcelorMittal Usibor® 22MnB5 Ultra high strength steel, Cold Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to .. |
|||
Tensile Strength, Ultimate | 1500 MPa | 218000 psi | after hot stamping |
ArcelorMittal Usibor® 22MnB5 Ultra high strength steel, Hot Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to .. |