Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Multibase Multi-Flex® TPE A 8592 MEDIUM TAUPE Heating aging the material 1000 hours at 125°C leads to a +7% change in the tensile strength, +4% change in elongation, and +12% change in tear strength. Ash is 16%. Multi-Flex TPE contains Krato.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | |
3M Dyneon™ Fluorel™ FC-2110Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Excellent processability. Viscosity .. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
ExxonMobil Escor® AT-310 EMAAA Terpolymer for Polymer Modification
(discontinued **) Data provided by the manufacturer, Exxon Chemical.45 Acid Number. Provides unusual adhesion to a variety of substrates and other components such as aluminum foil, polyolefins, polycarbonate, PET, e.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Total Finaprene® 435 Styrene-Butadiene TPE Copolymer
(discontinued **) Styrene-Butadiene CopolymerDescription: Finaprene® is a thermoplastic elastomer type radial styrene-butadiene block copolymer. Thanks to its medium molecular weight, Finaprene® 435 provides excel.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE 1008 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Superior strength, good machinability, and heat seal characteristics.Applications: Film extrusion: industrial packaging, frozen food, produce bags, shrink, a.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE1031 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Superior strength, good machinability, and heat seal characteristics.Applications: Film extrusion: clarity packaging, frozen food, produce bags, shrink, bund.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Chevron Phillips HiD® 9706 HDPE Injection Molding Resin
(discontinued **) Resin Type: linear homopolymerCharacteristics: moderate flow, good impact strength, excellent stiffness, good ESCR, moderate shrinkage resistanceApplications: crates and totes, structural foamInform.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE1205 EVA Film Extrusion
(discontinued **) 2% Vinyl Acetate EVA copolymer and FDA compliantFeatures: High clarity film with good stiffness and low temperature toughness.Applications: Film extrusion: food packaging, general purpose packaging .. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE 1402 EVA Film Extrusion
(discontinued **) 4% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Tensile Strength, Ultimate | 14.0 - 250 MPa @Temperature -40.0 - 250 °C |
2030 - 36300 psi @Temperature -40.0 - 482 °F |
Average value: 83.4 MPa Grade Count:3 |
Overview of materials for Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled". Specific grades with glass content between 25% an.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | IV, 2 in/min; ASTM D638 |
LyondellBasell Sequel® 1718 Engineered Polyolefin Data provided by Solvay Engineered Polymers.An engineered polyolefin designed for exterior painted automotive applications requiring dimensional stability over a broad temperature range. This mater.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
LyondellBasell Astryn SZ021-2 Polypropylene Copolymer, 20% Talc Key Features: medium melt flow, medium modulus, mineral-filled, utility grade polypropylene copolymer, good impact and stiffness balance, versatileApplications: inner door panels and seat supportsDe.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ISO R527-1 |
LyondellBasell Hifaxâ„¢ BB222GC Thermoplastic Olefin Resin Key Features: medium melt flow, very high modulus, UV-stabilized thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, excellent weatherability, high stiffness, good dimens.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | DIN 53504 |
Lubrizol ESTANE® T4086 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 260 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | butt tensile strength per ASTM D426 on brass |
Von Roll Isola IMI E-Solder® 3021 Electrically Conductive Adhesive Data provided by Von Roll Isola USA.E-SOLDER® epoxy based resin systems can be used at room temperature on heat sensitive materials, can bond dissimilar materials, and do not have flux or residue t.. |
|||
Tensile Strength, Ultimate | >= 14.0 MPa | >= 2030 psi | |
Von Roll Isola IMI Irrathene® 210 Irradiated Polyethylene Film, Encapsulation Grade Data provided by Von Roll Isola USA.Produced by electron bombardment of specially formulated polyethylene film used in a wide variety of electrical applications. Irrathene film is nonmelting and hi.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Toyobo Pelprene™ P-150M Polyester TPE Key Feature: Pelprene P typePelprene™ can be processed into a wide variety of articles from ultra-small precision parts to sheets by injection, extrusion, and blow molding. The 'P' type is a block.. |
|||
Tensile Strength, Ultimate | 14.0 MPa @Time 605000 sec |
2030 psi @Time 168 hour |
Heat Aging; ASTM D 412/ASTM D 573 |
Zylog Neoplast® 180 HOFR Thermoplastic Vulcanizate Neoplast 180 HOFR is a flame retardant thermoplastic vulcanizate (TPV) compound, based on polyolefin chemistry, suitable for Injection Molding and Extrusion applications.RoHS Compliant, UV Stabilize.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 750 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | GB/T 528 |
Chengdu Polyster 8500 General Grade TPV Information provided by Chengdu Polyster Co., Ltd. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638/D412 |
Covestro Baydur® 730 IBS Polyurethane Structural Foam RIM, Density 35 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience .. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
A. Schulman ComAlloy Comtuf® 109 Polypropylene, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | |
BASF Lucalen® A 2710 H Ethylene/Acrylate Copolymer Product with properties which are typical of flexible PVC and of low density polyethylene. Suitable for flexible pipes, profiles and seals.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE6010 Blow Molding Polyethylene
(discontinued **) Homopolymer, Drug Master File listed product, complies with USP Classification VI, and FDA compliant.Features: Meets exacting requirements of blow molded containers and processes well with parison s.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE7011 Profile Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Excellent strength, good machinability, and foaming characteristics.Applications: Extrusion: profile extrusion.FDA Notes: Conforms to FDA regulation 21 CFR 17.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
ExxonMobil Escorene® UL-7560 EVA Copolymer, Adhesive and Sealant Grade
(discontinued **) Data provided by the manufacturer, Exxon Chemical.An 18% vinyl acetate copolymerApplications: Hot melt adhesives; Wax blends; Industrial sealants. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ISO R527-1 |
LyondellBasell Hifax™ ETA-3163 Thermoplastic Olefin Resin Key Features: medium melt flow, medium high modulus, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, good dimensional stability, good paintability, good pro.. |
|||
Tensile Strength, Ultimate | 14.0 - 32.4 MPa | 2030 - 4700 psi | Average value: 26.4 MPa Grade Count:21 |
Overview of materials for Polypropylene with 40% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Mica Filler". Specific grades with primary filler content between 35% and 44% are.. |