Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 110 - 191 MPa | 16000 - 27700 psi | Average value: 156 MPa Grade Count:11 |
Overview of materials for Polyaryletherketone (PAEK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyaryletherketone (PAEK), Glass Fiber Filled". Each property range of values reported is minimum and m.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ISO 527 |
LATI LAESTRA E01 G/30 30% Glass Fiber Reinforced, Elastomer Modified Syndiotactic Polystyrene (SPS)
(disconti Description: Laestra compounds are syndiotactic polystyrene (SPS) products. SPS is a polymer offering a combination of properties unavailable with other materials. It exhibits a melting point of 270.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D882 |
Honeywell Capran® 980 Heat Stabilized Nylon Film
(discontinued **) Description: Capran® 980 is a clear (low haze level), heat-stabilized cast film produced from modified nylon 6 resin. Capran® 980 has excellent heat stability and resistance to pinholing. It ca.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
Global 508 30% Glass Filled PBT Gray Information provided by Global Polymers Corporation. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
Techmer ES Plaslube® J-1850/30/TF/15 PBT, 30% GFR, 15% PTFE |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
Techmer ES Plaslube® J-50/20/SI/2 Polycarbonate, 20% GFR, 2% Silicone |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ISO 527-1, 2 |
Polyplastics Duranex® 7300E Polybutylene Terephthalate (PBT), Conductive, GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
Zhejiang Double Fish YS-G030 30% Long Fiber Glass Reinforced Polypropylene Features high strength, good surface quality, and easy processing. Typical applications include automobile (bumper back beam, arm rest core, instrument panel, mudflap), machinery, electronics, comm.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ISO 527-1, 2 |
Polyplastics Duranex® C5315 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 15% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
DSM Novamid® 1010GH30 NAT PA6-GF30 30% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
DSM Novamid® 1013G30 1 NA PA6-GF30 30% Glass Reinforced, Injection Molding |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
DSM Stanyl® 46SF5030 PA46-GF30 FR(17) 30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow |
|||
Tensile Strength, Ultimate | 110 MPa @Temperature 120 °C |
16000 psi @Temperature 248 °F |
ISO 527-1/-2 |
DSM Stanyl® TS250F8 PA46-GF40 FR 40% Glass Reinforced, Flame Retardant, Heat Stabilized |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
DSM Stanyl® TW241B3 PA46-CF15 15% Carbon Reinforced, Heat Stabilized, Lubricated |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5 mm/min |
Arkema Group Orgalloy® RS 6015 EST Nylon 6 Alloy, 18% Glass Fiber (Conditioned) RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties... |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
Adell AT-14 Nylon 66, 20% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
Chem Polymer Chemlon 115 G Nylon 66, 15% Glass Fiber Reinforced A 15% glass fiber reinforced nylon 66 offering improved creep resistance, stiffness, tensile strength and dimensional stability over unmodified nylon 66 materials. This product offers slight improv.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 512 Polycarbonate, Glass Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
Adell AJ-14 Nylon 66, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 110 - 140 MPa | 16000 - 20300 psi | ASTM D638 |
Chang Chun Plastic PBT4130 Fire Retardant & 30% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 110 - 205 MPa | 16000 - 29700 psi | Average value: 159 MPa Grade Count:7 |
Overview of materials for Nylon 46, Lubricated + Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Lubricated + Glass Fiber Reinforced". Each property range of values reported is minimum and ma.. |
|||
Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
DSM Stanyl® TS200B3 PA46-CF15 15% Carbon Reinforced |
|||
Tensile Strength, Ultimate | 110 MPa @Temperature 180 °C |
16000 psi @Temperature 356 °F |
ISO 527-1/-2 |
DSM Stanyl® TS200F10 PA46-GF50 50% Glass Reinforced |
|||
Tensile Strength, Ultimate | 110 MPa @Temperature 120 °C |
16000 psi @Temperature 248 °F |
ISO 527-1/-2 |
DSM Stanyl® TS200F6 PA46-GF30 30% Glass Reinforced |