Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Peel Strength | 7.36 kN/m @Temperature 22.2 °C |
42.0 pli @Temperature 72.0 °F |
Bell Peel, Primed with Redux 119 |
Hexcel® Redux® 319 High Performance Modified Epoxy Film Adhesive (0.07 psf) Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported ve.. |
|||
Peel Strength | 7.36 kN/m @Temperature 60.0 °C, Time 605000 sec |
42.0 pli @Temperature 140 °F, Time 168 hour |
in JRF/SW, MIL-C-27725 |
3M AC-350 Class C-1/2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class C are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant hav.. |
|||
Peel Strength | 7.36 kN/m @Temperature 60.0 °C, Time 605000 sec |
42.0 pli @Temperature 140 °F, Time 168 hour |
in JRF/SW, MIL-PRF-85582 |
3M AC-350 Class C-1/2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class C are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant hav.. |
|||
Peel Strength | 7.36 kN/m @Temperature 60.0 °C, Time 605000 sec |
42.0 pli @Temperature 140 °F, Time 168 hour |
in JRF/SW, MIL-C-27725 |
3M AC-350 Class C-2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class C are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant hav.. |
|||
Peel Strength | 7.36 kN/m @Temperature 60.0 °C, Time 605000 sec |
42.0 pli @Temperature 140 °F, Time 168 hour |
in JRF/SW, MIL-PRF-85582 |
3M AC-350 Class C-2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class C are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant hav.. |
|||
Peel Strength | 7.36 kN/m @Temperature 60.0 °C, Time 605000 sec |
42.0 pli @Temperature 140 °F, Time 168 hour |
in JRF/SW, MIL-C-27725 |
3M AC-350 Class C-8(24) Aerospace Sealant 3M Aerospace Sealant AC-350 Class C are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant hav.. |
|||
Peel Strength | 7.36 kN/m @Temperature 60.0 °C, Time 605000 sec |
42.0 pli @Temperature 140 °F, Time 168 hour |
in JRF/SW, MIL-PRF-85582 |
3M AC-350 Class C-8(24) Aerospace Sealant 3M Aerospace Sealant AC-350 Class C are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant hav.. |
|||
Peel Strength | 7.36 kN/m @Temperature 24.0 °C, Time 432000 sec |
42.0 pli @Temperature 75.2 °F, Time 120 hour |
180°, Canvas/Steel |
3M Scotch-Weld™ 1357 Neoprene High Performance Contact Adhesive 3M™ Scotch-Weld™ Neoprene High Performance Contact Adhesive can be used to bond most rubber, cloth, metal, wood, foamed glass, paper honeycomb, decorative plastic laminates and many other substrat.. |
|||
Peel Strength | 7.36 kN/m @Temperature 24.0 °C, Time 432000 sec |
42.0 pli @Temperature 75.2 °F, Time 120 hour |
180°, Canvas/Steel |
3M Scotch-Weld™ 1357-L Neoprene High Performance Contact Adhesive 3M™ Scotch-Weld™ Neoprene High Performance Contact Adhesive can be used to bond most rubber, cloth, metal, wood, foamed glass, paper honeycomb, decorative plastic laminates and many other substrat.. |