Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Peel Strength | 4.21 kN/m @Temperature 80.0 °C |
24.0 pli @Temperature 176 °F |
Floating Roller Peel |
Hexcel® Redux® 610W (0.03 psf) Flame retarded epoxy film adhesive Redux 610 is a modified, flame-retarded epoxy film adhesive curing at 250°F. It is suitable for bonding metal to metal and for sandwich structures where flame retardancy and low heat release are re.. |
|||
Peel Strength | 4.21 kN/m @Temperature 60.0 °C, Time 605000 sec |
24.0 pli @Temperature 140 °F, Time 168 hour |
JRF/SW, MIL-C-27725; AMS-S83318 |
3M AC-250 A-1/6 Aerospace Sealant 3M Aerospace Sealant AC-250 A-1/6 is a two-part, low temperature curing polysulfide, quick repair sealant for integral fuel tank and fuselage sealing applications. The mixed compound is a pourable l.. |
|||
Peel Strength | 4.21 kN/m @Temperature 60.0 °C, Time 605000 sec |
24.0 pli @Temperature 140 °F, Time 168 hour |
JRF/SW, Alclad; AMS-S83318 |
3M AC-250 A-1/6 Aerospace Sealant 3M Aerospace Sealant AC-250 A-1/6 is a two-part, low temperature curing polysulfide, quick repair sealant for integral fuel tank and fuselage sealing applications. The mixed compound is a pourable l.. |
|||
Peel Strength | 4.21 kN/m @Temperature 24.0 °C, Time 1.21e+6 sec |
24.0 pli @Temperature 75.2 °F, Time 336 hour |
180°, Canvas/Steel |
3M Scotch-Weld™ 1357 Neoprene High Performance Contact Adhesive 3M™ Scotch-Weld™ Neoprene High Performance Contact Adhesive can be used to bond most rubber, cloth, metal, wood, foamed glass, paper honeycomb, decorative plastic laminates and many other substrat.. |
|||
Peel Strength | 4.21 kN/m @Temperature 24.0 °C, Time 1.21e+6 sec |
24.0 pli @Temperature 75.2 °F, Time 336 hour |
180°, Canvas/Steel |
3M Scotch-Weld™ 1357-L Neoprene High Performance Contact Adhesive 3M™ Scotch-Weld™ Neoprene High Performance Contact Adhesive can be used to bond most rubber, cloth, metal, wood, foamed glass, paper honeycomb, decorative plastic laminates and many other substrat.. |
|||
Peel Strength | 4.21 kN/m @Temperature 66.0 °C, Time 1.81e+6 sec |
24.0 pli @Temperature 151 °F, Time 504 hour |
180°, Canvas/Steel |
3M Scotch-Weld™ 2141 Neoprene Rubber & Gasket Adhesive Features: Alight colored, high strength adhesive with a long tack rangeExcellent water, oil and grease resistanceBonds neoprene, natural, reclaim SB-R and butyl rubber to most substrates.Information.. |
|||
Peel Strength | 4.21 kN/m @Temperature 24.0 °C, Time 432000 sec |
24.0 pli @Temperature 75.2 °F, Time 120 hour |
180°, Canvas/Steel |
3M Scotch-Weld™ 2141 Neoprene Rubber & Gasket Adhesive Features: Alight colored, high strength adhesive with a long tack rangeExcellent water, oil and grease resistanceBonds neoprene, natural, reclaim SB-R and butyl rubber to most substrates.Information.. |
|||
Peel Strength | 4.21 kN/m @Temperature 24.0 °C, Time 259000 sec |
24.0 pli @Temperature 75.2 °F, Time 72.0 hour |
180°, Canvas/Steel |
3M Fastbond™ 4213-NF Industrial Adhesive 3M™ Fastbond™ Industrial Adhesive 4213-NF is a white, water dispersed adhesive for bonding many fabrics, supported vinyl, wood, leather and most porous materials. Exhibits outstanding clarity when.. |
|||
Peel Strength | 4.21 kN/m @Temperature 24.0 °C, Time 259000 sec |
24.0 pli @Temperature 75.2 °F, Time 72.0 hour |
180°, Canvas/Steel |
3M Scotch-Weld™ 4475 Industrial Adhesive Features: Dries quickly to a firm bondExcellent resistance to water, plasticizer migration, many detergent and soap solutions, oils and greasesA general purpose adhesive for bonding most vinyls, cer.. |