Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 73.5 MPa @Temperature 110 °C |
10700 psi @Temperature 230 °F |
Cold Crushing |
Sharadaa Ceramics REFCAST LC45 Low Cement Castables Description: We bring to our clients a range of Low Cement Castables, that are available in varied alumina content and service range. Designed for abrasion resistance application, these are widely u.. |
|||
Compressive Strength | 73.5 MPa @Temperature 1100 °C |
10700 psi @Temperature 2010 °F |
Cold Crushing |
Sharadaa Ceramics ZAP 006 Smart Cast Application Special Properties: Thermal Shock, Flame ErosionIndustry: Multi PurposeApplication: Burner Blocks all types of Thermal Shock ApplicationsInformation provided by Sharadaa Ceramics Pvt. Ltd. |
|||
Compressive Strength | >= 73.5 MPa @Temperature 110 °C |
>= 10700 psi @Temperature 230 °F |
Cold Crushing |
Sharadaa Ceramics VELCRETE G 401 Gunning Castables Description: Available from us a range of Gunning Castables that are made in compliance with the set industrial standards. These castables are widely used in refineries, foundries, boilers, rolling .. |
|||
Compressive Strength | 73.5 MPa @Temperature 1100 °C |
10700 psi @Temperature 2010 °F |
Cold Crushing |
Sharadaa Ceramics ZAP 012 Smart Cast Application Special Properties: Patching At Hot Conditions, Easy InstallationIndustry: All IndustryApplication: All type of Rotary Kilns, AL/CU Melting Furnaces, Rolling Mills, Forgoing Furnaces, IncineratorsIn.. |
|||
Compressive Strength | 73.5 MPa @Temperature 1350 °C, Time 10800 sec |
10700 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength |
Chosun Refractories MMCT-95 Special Castable Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET). |
|||
Compressive Strength | 73.5 MPa @Temperature 110 °C, Time 86400 sec |
10700 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
Chosun Refractories SCX-50KL Special SiC Castable Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET). |