Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 668.8 MPa @Thickness 1.60 - 4.70 mm, Temperature 316 °C |
97000 psi @Thickness 0.0630 - 0.185 in, Temperature 601 °F |
|
Haynes Hastelloy® C-276 alloy, solution heat treated flat products Hastelloy® C-276 alloy is a nickel-molybdenum-chromium wrought alloy that is a versatile corrosion-resistant alloy. C-276 alloy is an improved wrought version of alloy C in that it usually doesn'.. |
|||
Tensile Strength, Ultimate | 669 MPa @Thickness 25.4 mm |
97000 psi @Thickness 1.00 in |
Longitudinal Direction |
Alcoa 7055-T7751 Aluminum Plate Alcoa introduced alloy 7055 in the -T7751 temper for plate and the -T77511 for extrusions in 1991. This alloy was developed for use in compression-dominated structures (such as upper wing structures.. |
|||
Tensile Strength, Ultimate | 669 MPa @Thickness 3.20 mm, Temperature 427 °C |
97000 psi @Thickness 0.126 in, Temperature 801 °F |
|
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |