Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 1140 MPa @Temperature 550 °C |
165000 psi @Temperature 1020 °F |
Precipitation Hardened prior to test |
Special Metals INCOLOY® Alloy 907 A nickel-iron-cobalt alloy with additions of niobium and titanium for precipitation hardening. It has the low coefficient of expansion and high strength of INCOLOY alloy 903 but with improved notch.. |
|||
Tensile Strength, Ultimate | 1140 MPa @Temperature 550 °C |
165000 psi @Temperature 1020 °F |
Precipitation Hardened prior to test |
Special Metals NIMONIC® Alloy 115 A precipitation-hardenable nickel-chromium-cobalt alloy with an addition of molybdenum for solid-solution strengthening. It is similar to NIMONIC alloy 105 but has higher levels of aluminum and tit.. |
|||
Tensile Strength, Ultimate | 1140 MPa @Temperature 23.0 °C |
165000 psi @Temperature 73.4 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 201L, 20% Cold Work (UNS S20103) Allegheny Ludlum Types 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201L provides advantages over the 18-8 grades in certain applications. Lower cost manganese .. |