Polymer Property : Tensile Strength, Ultimate = 133000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	918 MPa @Thickness 1.45 mm	133000 psi @Thickness 0.0571 in
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate	914 MPa @Thickness 1.45 mm	133000 psi @Thickness 0.0571 in
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate	917 MPa @Thickness 12.7 mm, Temperature 20.0 Â°C	133000 psi @Thickness 0.500 in, Temperature 68.0 Â°F
Haynes UltimetÂ® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate	920 MPa @Thickness 1.45 mm	133000 psi @Thickness 0.0571 in
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..