Polymer Property : Flexural Yield Strength = 9430 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycolac® INP564 ABS SABIC INP564 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet..
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycolac® INP564 ABS+SAN SABIC INP564 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet..
Flexural Yield Strength	65.0 MPa	9430 psi	DIN 53452
Ineos Nova S-5400 High Impact Compact Polystyrene (discontinued **) Impact polystyrene with high dimensional stability under heat, particularly suitable fore extrusion and thermoforming of technical parts or packaging applications but also used for injection molding..
Flexural Yield Strength	65.0 - 234 MPa	9430 - 34000 psi	Average value: 146 MPa Grade Count:71
Overview of materials for Acetal Copolymer, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Carbon Fiber Filled". Each property range of values reported is minimum and maximum va..
Flexural Yield Strength	65.0 MPa @Strain 3.50 %	9430 psi @Strain 3.50 %	2 mm/min; ISO 178-A
Lanxess PocanÂ® DP C 1502 000000 PBT + PC PBT + PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, UV-stabilizedInformation provided by LANXESS.
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL V090 PPE+HIPS (Europe-Africa-Middle East) NORYL V090 is an unfilled, flame retardant material with a Vicat B/120 of 95 Â°C according ISO 306. NORYL V090 is V0 at 2.0 mm and V1 at 1.6 mm according UL94 and halogen free according VDE/DIN 47..
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KL003E POM (Europe-Africa-Middle East) LNP* LUBRICOMP* KL003E is a compound based on Acetal Copolymer resin containing PTFE. Added features include: Internally Lubricated, Easy Molding.
Flexural Yield Strength	65.0 MPa	9430 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® V2105U PBT Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio.
Flexural Yield Strength	65.0 MPa	9430 psi	ASTM D790
Spartech Royalite R60M Hi-Impact ABS/PVC Resin Data provided by the manufacturer. This rigid, fire-rated, proprietary resin is specifically formulated to meet the requirements of the FAR 25.853 A flammability test. Primary applications are air..
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics XenoyÂ® CL402 PBT+PC (Europe-Africa-Middle East) XENOY CL402 is a high viscosity, unfilled, elastomer modified PC/PBT blend for extrusion/blowmolding applications. ISO1043-label: PC+PBT-I.This data was supplied by SABIC-IP for the Europe-Africa-Mi..
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics XenoyÂ® CL402U PBT+PC (Europe-Africa-Middle East) XENOY CL402U has been specially developed for extrusion blowmoulding applications, where higher melt strength is desired. XENOY CL402U is a high impact material combined with good UV resistance perf..
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp MCR13S PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MCR13S is a compound based on Polypropylene resin containing Carbon Fiber, Barium Sulfate. Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-..
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Noryl HF180 PPE+HIPS (Europe-Africa-Middle East) NORYL HF180 is an unfilled, flame retardant material with a Vicat B/120 of 100Â°C according ISO 306. NORYL HF180 is V1 at 2.0 mm according UL94 and halogenThis data was supplied by SABIC-IP for th..
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL PVX516 PPE PREVEX* PVX516 resin is a high flow, non FR grade, 110 C HDT
Flexural Yield Strength	65.0 MPa	9430 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility
Flexural Yield Strength	65.0 MPa	9430 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Asia Pacific) PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility
Flexural Yield Strength	65.0 MPa	9430 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Europe-Africa-Middle East) PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL 725A PPE+HIPS (Europe-Africa-Middle East) NORYL 725A is an unfilled material, with a Vicat B/120 of 135Â°C according ISO 306. NORYL 725A has been designed for use in automotive interior applications, where anti-squeak is required.
Flexural Yield Strength	65.0 MPa	9430 psi	ASTM D790
Tipco Tipcolite® TG 311 Phenolic Compound, Mineral & Wood Flour, Medium Flow & High Electrical Properties Medium Flow Phenolic Compound, Reinforced with Mineral & Wood FlourApplications: Electrical & ElectronicsProcessing: Compression & TransferInformation provided by the Manufacturer, Tipco Industrie..
Flexural Yield Strength	65.0 MPa	9430 psi	ASTM D790
Tipco Tipcolite® TG 615 Phenolic Compound, Mineral & Wood Flour, Medium Flow & High Electrical Properties Medium Flow Phenolic Compound, Reinforced with Mineral & Wood FlourApplications: Electrical & ElectronicsProcessing: Compression & TransferInformation provided by the Manufacturer, Tipco Industrie..
Flexural Yield Strength	65.0 MPa	9430 psi	ASTM D790
Eastman Tenite Butyrate 264E0096908 Natural, Trsp Cellulose Acetate Butyrate Plasticizer 22%. Weight loss on heating = 0.5% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
Eurostar Staramide P1000IX1 PA6, Impact Modified, Injection Molded Staramide P1000IX1 is an Impact Modified, Polyamide 6 Injection Molding Resin (also known as P1000HI006 or Star X 2006)Information provided by Eurostar.
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
Eurostar Starpylen MCR13S PP, 15% Carbon Fiber Filled, Injection Molded Starpylen MCR13S is a 15% Carbon Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
Flexural Yield Strength	65.0 - 268 MPa	9430 - 38900 psi	Average value: 99.2 MPa Grade Count:30
Overview of materials for Nylon 6, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, PTFE Filled". Each property range of values reported is minimum and maximum values of appropria..
Flexural Yield Strength	65.0 MPa	9430 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL EM6100 PPE+PS (Asia Pacific) Medium heat, high impact PPO/HIPS alloy used in the automotive industry.
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL PX2355 PPE+HIPS (Europe-Africa-Middle East) NORYL PX2355 is an unfilled, medium heat, low odour and low emission material with excellent heat aging performance. It has been developed for automotive interior applications, such as instrument pa..
Flexural Yield Strength	65.0 MPa	9430 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Valox® V2105U PBT (Asia Pacific) Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio.
Flexural Yield Strength	65.0 MPa @Strain 3.50 %	9430 psi @Strain 3.50 %	2 mm/min; ISO 178-A
Lanxess Pocan® C 1206 000000 PET + PC PET + PC, non-reinforced, injection molding, improved impact strengthInformation provided by LANXESS.
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® CP8320 PC+ABS (Asia Pacific) Cycoloy Medium Heat Plating Grade for Automotive
Flexural Yield Strength	65.0 MPa	9430 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Valox® VX3608C PBT (Europe-Africa-Middle East) VALOX VX3608C is an impact modified, flame retardant PBT+PC injection moulding resin. Application: electrical enclosures. This grade is 3607U with reduced oxygen index.This data was supplied by SABI..