Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 63.7 - 92.2 MPa | 9250 - 13400 psi | Average value: 85.4 MPa Grade Count:6 |
Overview of materials for PEN-PET This property data is a summary of similar materials in the MatWeb database for the category "PEN-PET". Each property range of values reported is minimum and maximum values of appropriate MatWeb ent.. |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
15 mm/min; ASTM D790 |
LG Chemical AF342T ABS, Flame Retardant, High Impact Feature: Injection Molding, Flame Retardant, High ImpactApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9, 40039-93-8 and 1309-64-4Information provide.. |
|||
Flexural Yield Strength | 63.7 MPa | 9250 psi | DIN 53455; ASTM D790 |
Kolon NOPLA® KE531HC PEN-PET Copolyester NOPLA® is an advanced PEN-PET copolyester which can be used for bottle, sheet & injection molding applicationsUV protection & prolonged outdoor durability, enhanced gas barrier, outstanding impac.. |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 3.20 mm |
9250 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical SH610A ABS, High Impact Feature: Extrusion Molding, General Purpose, High ImpactApplication: Bag, Automobile InteriorCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
Iran Petrochemical (PCC) SH-0150 Acrylonitrile Butadiene Styrene SH - 0150 ABS extrusion grade has been formulated to provide excellent mechanical properties,extrusion stability, vacuum formability and chemical resistance. It is a high flow extrusion grade with h.. |
|||
Flexural Yield Strength | 63.7 MPa @Temperature 23.0 °C |
9250 psi @Temperature 73.4 °F |
ASTM D790 |
IRPC Polimaxx Porene KU650 Acrylonitrile Butadiene Styrene Applications:injection moldingautomotive parts such as instrument panels, console boxes, switches, automotive louvers, ectelectrical appliances |
|||
Flexural Yield Strength | 63.7 MPa @Temperature 23.0 °C |
9250 psi @Temperature 73.4 °F |
ASTM D790 |
IRPC Polimaxx Porene SP100 Acrylonitrile Butadiene Styrene Applications:injection moldinghelmetsautomotive |
|||
Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
Lendell Parapet GR-00100 PMMA, High Impact |
|||
Flexural Yield Strength | 63.8 MPa | 9250 psi | |
Haveg 61NA Furfuryl Alcohol-Formaldehyde Resin A proprietary thermoset plastic consisting of a furfuryl alcohol-formaldehyde resin and non-asbestos silicate fillers. |
|||
Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
Samyang Triloy® 120H PC/ABS alloy Characteristics:Impact resistantChemical resistantDimensional stabilityProcessabilityGood flowApplications:Automotive bumperAutomotive outdoor handleAll information provided by Samyang |
|||
Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
Cheng Yu Plastic ML849 Flame Retardant PC |
|||
Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
Cheng Yu Plastic PP226 Flame Retardant Polypropylene, Medium Impact |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron HI40I ABS Injection Molding Grade Automotive applications -Super High Impact , High Rigidity, PaintableInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-11B ABS Injection Molding Grade High Impact Strength, Medium Flow, High Fatigue ResistanceInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron IM17A TT ABS Injection Molding Grade High Flow, Medium ImpactInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
ASTM D790 |
Bhansali Engineering Abstron MIF-45 ABS Injection Molding Grade High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron SE45I Extrusion ABS Very High Impact, Low Flow, High Rigidity and Sheet/Pipe/Profile applicationInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron IM17V ABS Injection Molding Grade Super High Gloss, Medium ImpactInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
ASTM D790 |
Bhansali Engineering Abstron MIF-35 ABS Injection Molding Grade High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron MIF45EP ABS Injection Molding Grade Electroplating, High FlowInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron SE45I Extrusion ABS Very High Impact, Low Flow, High Rigidity and Sheet/Pipe/Profile applicationInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
Cheng Yu Plastic IPS601 Flame Retardant HIPS |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-11B ABS Injection Molding Grade High Impact Strength, Medium Flow, High Fatigue ResistanceInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
Samyang Trimma® SD6350T PMMA, Opaque High scratch resistance; stability against weak acids, strong acids, weak alkalis and inorganic salts.Information provided by Samyang. |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron IM17V ABS Injection Molding Grade Super High Gloss, Medium ImpactInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron IM17A TT ABS Injection Molding Grade High Flow, Medium ImpactInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron IM21G ABS Injection Molding Grade Super High Gloss, Medium ImpactInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa @Thickness 6.40 mm |
9250 psi @Thickness 0.252 in |
ASTM D790 |
Bhansali Engineering Abstron MIF-45 ABS Injection Molding Grade High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali |
|||
Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
Cheng Yu Plastic IPS620BK Electric Conducting HIPS, Injection |
|||
Flexural Yield Strength | 63.7 MPa | 9250 psi | ASTM D790 |
Cheng Yu Plastic IPS666N Electric Resisting HIPS |