Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 39.0 MPa | 5660 psi | ASTM D790 |
Nylene® 609 Nylon 6, 50% RH, Film/Extrusion Grade Film Grade. Nylene 609 is a high viscosity, extrusion resin recommended for practically all types of extrusion including profile, film, and extrusion coating. It is especially recommended for
fl.. |
|||
Flexural Yield Strength | 39.0 MPa | 5660 psi | ASTM D790 |
North Wood Plastics Polypropylene with 60% Wood Fiber, Molding Grade Data provided by North Wood Plastics, Inc. |
|||
Flexural Yield Strength | 39.0 MPa | 5660 psi | ASTM D790 |
Rotuba MH Cellulose Acetate Property values at 50% RH.Data provided by the manufacturer. |
|||
Flexural Yield Strength | 39.0 - 106 MPa | 5660 - 15400 psi | Average value: 80.3 MPa Grade Count:65 |
Overview of materials for Polystyrene, Heat Resistant Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Heat Resistant Grade". Each property range of values reported is minimum and maximum values.. |
|||
Flexural Yield Strength | 39.0 MPa | 5660 psi | ASTM D790 |
Ineos Nova 5751 High Impact Polystyrene
(discontinued **) High flow, Good impact, USP Class VIApplications: Single service impact, Medical, Housewares, CompoundingProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwi.. |
|||
Flexural Yield Strength | 39.0 MPa | 5660 psi | 2 mm/min; ASTM D790 |
Solvay Specialty Polymers Solef® 1015/0078 PVDF Homopolymer
(discontinued **) Key features of this grade: Plasticized, Offshore, Piping, Formulated. Recommended processing is extrusion. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorina.. |
|||
Flexural Yield Strength | 39.0 - 276 MPa | 5660 - 40000 psi | Average value: 101 MPa Grade Count:94 |
Overview of materials for Nylon 66, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum .. |
|||
Flexural Yield Strength | 39.0 MPa | 5660 psi | ASTM D790 |
Tipco Tipcolene® FPT 30 BK CP - 30% Talc Polypropylene Homopolymer, Special Heat Stability 30% Talc Reinforced PP Homopolymer with Special AdditivesApplications: AutomotivesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Flexural Yield Strength | 39.0 MPa | 5660 psi | ASTM D790 |
Covestro Baydur® 726 IBS Polyurethane Structural Foam RIM, Density 40 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience .. |
|||
Flexural Yield Strength | 39.0 MPa | 5660 psi | ASTM D790 |
Covestro Baydur® STR/F-375 Polyurethane Composite SRIM Foam, 20% Glass Filled, MDI-based 2-Component Liquid System Contains continuous strand fiberglass mat.0.125 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer .. |