Polymer Property : Flexural Yield Strength = 30500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	210 MPa	30500 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Opnyl OP66GF33 Nylon 66, 33% Glass Reinforced, Dry Nylon 66 - Glass reinforced (33 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the ..
Flexural Yield Strength	210 MPa	30500 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Faradex DX07304 PC (Asia Pacific) CF filled grade with EMI shieldingThis data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Yield Strength	210 MPa @Strain 3.50 %	30500 psi @Strain 3.50 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 50 000000 Nylon 6, Glass Fiber Reinforced PA 6, 50% glass fibers, injection moldingInformation provided by LANXESS.
Flexural Yield Strength	210 MPa @Strain 3.50 %	30500 psi @Strain 3.50 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® AKV 40 H3.0 000000 Nylon 66, Glass Fiber Reinforced PA 66, 40% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS.
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem 2200N PEI (Asia Pacific) 20% Glass fiber filled Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem 2200N PEI (Europe-Africa-Middle East) 20% Glass fiber filled Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2210F PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2210K PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2210K PEI (Asia Pacific) 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem 2210K PEI (Europe-Africa-Middle East) 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2310EPR PEI 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM HU2210 PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP ..
Flexural Yield Strength	210 MPa	30500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON DE0069F PC LNP* STAT-KON* DE0069F is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Superior Molding.
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 8032UX PBT+PET (Europe-Africa-Middle East) VALOX 8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX 8032U with improved weathering resistance. Applications: appliance housin..
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® IQ420 PBT Environmentally responsible Valox iQ420 resin: iQ-PBT+ 30% glass fiber reinforcement. Targeted for use in electrical motors, connectors, pump housings, spotlights, appliance handles, etc.
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® IQ420 PBT (Asia Pacific) Environmentally responsible Valox iQ420 resin: iQ-PBT+ 30% glass fiber reinforcement. Targeted for use in electrical motors, connectors, pump housings, spotlights, appliance handles, etc.
Flexural Yield Strength	210 MPa	30500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® IQ420 PBT (Asia Pacific) Environmentally responsible Valox iQ420 resin: iQ-PBT+ 30% glass fiber reinforcement. Targeted for use in electrical motors, connectors, pump housings, spotlights, appliance handles, etc.
Flexural Yield Strength	210 MPa	30500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® IQ420 PBT (Europe-Africa-Middle East) Environmentally responsible Valox iQ420 resin: iQ-PBT+ 30% glass fiber reinforcement. Targeted for use in electrical motors, connectors, pump housings, spotlights, appliance handles, etc.
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® IQ420 PBT (Europe-Africa-Middle East) Environmentally responsible Valox iQ420 resin: iQ-PBT+ 30% glass fiber reinforcement. Targeted for use in electrical motors, connectors, pump housings, spotlights, appliance handles, etc.
Flexural Yield Strength	210 MPa	30500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® IQ420HP PBT (Asia Pacific) Environmentally responsible, low carbon footprint Valox iQ* resin - Valox* iQ420HP resin is made using iQ-PBT resin and 30% glass fiber reinforcement. Valox* iQ420HP may be used for the production..
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® V9260CS PET (Asia Pacific) Color Stable Glass filled PET
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® V9260DCS PET (Europe-Africa-Middle East) Color Stable Glass Filled PET (for Dark colors only)
Flexural Yield Strength	210 MPa	30500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® IQ420HP PBT Environmentally responsible, low carbon footprint Valox iQ* resin - Valox* iQ420HP resin is made using iQ-PBT resin and 30% glass fiber reinforcement. Valox* iQ420HP may be used for the production..
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® IQ420HP PBT Environmentally responsible, low carbon footprint Valox iQ* resin - Valox* iQ420HP resin is made using iQ-PBT resin and 30% glass fiber reinforcement. Valox* iQ420HP may be used for the production..
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® IQ420HP PBT (Europe-Africa-Middle East) Environmentally responsible, low carbon footprint Valox iQ* resin - Valox* iQ420HP resin is made using iQ-PBT resin and 30% glass fiber reinforcement. Valox* iQ420HP may be used for the production..
Flexural Yield Strength	210 MPa	30500 psi	ASTM D790
Tipco Tipcofil® AG 600 - 30% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability 30% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Flexural Yield Strength	210 MPa	30500 psi	ASTM Data
BASF Capron® 8232G HS FR BK-102 25% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron 8232G HS FR BK-102 is a 25% glass fiber reinforced, heat stabilized, flame retardant pigmented black nylon 6 injection molding compound exhibiting excellent melt stability characteristics. I..
Flexural Yield Strength	210 MPa	30500 psi	ASTM Data
BASF Capron® 8234G 44% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron 8234G is a 44% glass fiber reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stability. It is ..
Flexural Yield Strength	210 MPa	30500 psi	ASTM Data
BASF Capron® 8332G Impact Modified, 25% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron 8332G is a 25% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance of ..
Flexural Yield Strength	210 MPa	30500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOTUF OF008EI PPS (Europe-Africa-Middle East) LNP* Thermotuf* OF008EI is a compound based on PPS-Linear resin, containing Glass Fiber. Added features include : High Impact and Easy Molding.