Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 207 MPa | 30000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP 9X98026 PA 46 (Europe-Africa-Middle East) LNP* Lubricomp* 9X98026 is a compound based on PA4.6 resin containing Barium Sulfate, PTFE and Carbon Fiber |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFP36XXZ PA 66 (Asia Pacific) LNP Lubricomp RFP36XXZ is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: internally lubricated. Also known as Lubricomp RFL-4536 .. |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP DX10313 PC (Asia Pacific) DX10313 is high modulus polycarbonate, 50% glass filled, with balanced flow and impact strength |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Europe-Africa-Middle East) 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.This data was supplied by SABIC-IP for the Europe-Afr.. |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP 9X94104 PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* 9X94104 is a compound based on Polyetherimide resin containing Glass Fiber. |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
Techmer ES HiFill® TPX-HTN-01033 A 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: Heat StabilizerFeatures: Heat Stabilized and High Temperature StrengthUL File .. |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
Techmer ES HiFill® TPX-HTN-03003 A 40% Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler, 40% Filler by WeightFeatures: Platable and High Temperature StrengthUL File Number: E157318Information provided by TP C.. |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
Techmer ES Plastiblend® PA6 GF20 RM BK Nylon 6 Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber ReinforcementProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
Clariant PA213N40 Nylon 6, Mineral/Glass Reinforced, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
Clariant Renol BR2065 Nylon 66, Mineral/Glass Reinforced Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
Clariant Renol 6622-L Nylon 66, Glass Fiber Filled, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
Chem Polymer Durlex 740 G PBT, 40% Short Glass Fiber Reinforced A 40% short glass fiber reinforced PBT, offering a combination of excellent dimensional stability with high heat resistance and stiffness.Data provided by the manufacturer, Chem Polymer. |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
A. Schulman ComAlloy E-17099B Nylon 6/6, Electrically Conductive - Carbon Fiber Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | ASTM D790 |
PolyOne Stat-Tech™ RA-06CF-09GF/000 Polyarylsulfone - 9% Glass Fiber - 6% Carbon Fiber Reinforced - ESD Applications
&a Data provided by PolyOne. |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem ATX103R PEI+PCE 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.This data was supplied by SABIC-IP for the Americas r.. |
|||
Flexural Yield Strength | 207 MPa | 30000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Asia Pacific) 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.This data was supplied by SABIC-IP for the Asia Pacif.. |