Polymer Property : Flexural Yield Strength = 26100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Opnyl OP6GF43 Nylon 6, 43% Glass Reinforced, Conditioned Nylon 6 - Glass reinforced (43 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m..
Flexural Yield Strength	180 MPa	26100 psi	ISO 178, ASTM D790
Nilit Nilitop BT G6 FR C3 is a 30% Glass Fiber Reinforced, Flame Retardant PBT Description: Nilitop BT G6 FR C3 is a 30% glass fiber reinforced, flame retardant PBT with halogens. The flame retardant does not contain PBB and PBDE, so it is compliant with the WEEE directive. It..
Flexural Yield Strength	180 - 530 MPa	26100 - 76900 psi	Average value: 331 MPa Grade Count:50
Overview of materials for Polyphthalamide (PPA), Carbon Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Carbon Fiber". Each property range of values reported is minimum and maximum values of ..
Flexural Yield Strength	180 MPa @Temperature 90.0 °C	26100 psi @Temperature 194 °F	ISO 178, ASTM D790
Nilit Nilamid A3 H G7 General Purpose 35% Glass Reinforced PA66 Description: Nilamid A3 H G7 is a general purpose 35% glass fiber reinforced NYLON 66 that gives an excellent combination of tensile strength, stiffness and impact strength. It is one of the most wi..
Flexural Yield Strength	180 - 385 MPa	26100 - 55800 psi	Average value: 262 MPa Grade Count:50
Overview of materials for Polyetherimide (PEI), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, Carbon Fiber Filled". Each property range of values reported is minimum and maximum valu..
Flexural Yield Strength	180 MPa	26100 psi	ASTM D570
Radici Radilon® N66-ARV300FR Nylon 66 (discontinued **)
Flexural Yield Strength	180 MPa @Strain 3.50 %	26100 psi @Strain 3.50 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® AKV 35 HR H2.0 901510 Nylon 66, Glass Fiber Reinforced PA 66, 35% glass fibers, injection molding, heat-aging stabilized, hydrolysis stabilizedInformation provided by LANXESS.
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP KFI15 ACETAL LNP* LUBRICOMP* KFI15 is a compound based on Acetal containing 25% Glass Fiber, 2% Silicone. Added feature of this grade is: Wear Resistant.
Flexural Yield Strength	180 MPa	26100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP QFL36 PA6.10 (Europe-Africa-Middle East) LNPLubricomp QFL36 is a compound based on PA 6/10 resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated.
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE 50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. ECO Conforming.
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Asia Pacific) 50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. ECO Conforming.
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Europe-Africa-Middle East) 50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. RoHS compliant.
Flexural Yield Strength	180 MPa	26100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM AUR200G6 PEI (Europe-Africa-Middle East) The data listed in this data sheet are the lower specification limits, apart from the MFR, CTE, HDT at 1.8 MPa, Density, Tensile strain, Water Absorption, Thermal Conductivity and Shrinkage which ar..
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 5031 PBT (Europe-Africa-Middle East) VALOX 5031 is a 30% glass reinforced PBT+PC blend with low warpage characteristics. Applications: appliance handles, automotive doorhandles. This grade is a 508 with reduced warpage.
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® ENH4565 PBT (Asia Pacific) 33% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin, Good thermal shock resistance and low CTE.
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® ENH4565 PBT (Europe-Africa-Middle East) 33% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin, Good thermal shock resistance and low CTE.
Flexural Yield Strength	180 MPa	26100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® IQ4860HR PBT Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified.
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® IQ4860HR PBT (Asia Pacific) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified.
Flexural Yield Strength	180 MPa	26100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® IQ4860HR PBT (Asia Pacific) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified.
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® IQ4860HR PBT (Europe-Africa-Middle East) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified.
Flexural Yield Strength	180 MPa	26100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® IQ4860HR PBT (Europe-Africa-Middle East) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified.
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP DF005 PC LNP* Thermocomp* DF005 is a compound based on Polycarbonate containing 25% Glass Fiber.
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® EXVX1403 PBT (Asia Pacific) 33% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin, Good thermal shock resistance and low CTE.
Flexural Yield Strength	180 MPa	26100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN3 PPE+PS PPE+PS blend. 30% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Sui..
Flexural Yield Strength	180 MPa	26100 psi	ASTM D790
Clariant Renol BR7039G30 Nylon 6, 30% Glass Fiber, bondable to TPU Data provided by Clariant Masterbatches
Flexural Yield Strength	180 MPa	26100 psi	ASTM D790
E-Polymers TEKANATE™ G730 , 30% Glass Fiber Reinforced Poly Carbonate 30% Glass Fiber reinforcedInformation provided by E-Polymers Co. Ltd.
Flexural Yield Strength	180 MPa	26100 psi	ASTM D790
E-Polymers TEKANATE™ G730FR , Flame Retardant, 30% Glass Fiber Reinforced Poly Carbonate 30% Glass Fiber reinforced, Flame RetardantInformation provided by E-Polymers Co. Ltd.
Flexural Yield Strength	180 MPa	26100 psi	DIN 53 452
Albis Plastics Tedur® L 9523 PPS, 60% Glass Fiber/Mineral Extremely Rigid, Excellent Surface Finish, Metallization w/o Base Coating. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Insulating Equipment, Reflectors and Fitting..
Flexural Yield Strength	180 MPa	26100 psi	ASTM D790
E-Polymers TEKAMID® TA210G15 , 15% Glass Fiber Reinforced PA66, DAM Beautiful surface, strength propertyInformation provided by E-Polymers Co. Ltd.