Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 177 MPa | 25700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36E PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DFL36E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features include; Internally Lubricated, Easy Molding. |
|||
Flexural Yield Strength | 177 - 420 MPa | 25700 - 60900 psi | Average value: 331 MPa Grade Count:45 |
Overview of materials for Polyphthalamide (PPA), 50% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 50% Glass Fiber Reinforced". Each property range of values reported is minimum and maxi.. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | ASTM D790 |
Plenco 51240 PET, Pellet, Injection Molded, Black
(discontinued **) PLENCO 51240 is an engineering grade glass reinforced flame retarded recycled polyethylene terephthalate resin designed for excellent dimensional stability. It is UL listed.Information supplied by P.. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | DIN 53452; ASTM D790 |
Kolon Kopa® KN163G30 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT LNP LUBRICOMP* WFL34H is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Healthcare. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON RFD03 PA 66 LNP* STAT-KON* RFD03 is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this material is: Electrically Conductive. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF004ER PES (Europe-Africa-Middle East) LNP* Thermocomp* JF-1004 S-3 is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® SHF4960 PBT (Europe-Africa-Middle East) Valox Super high flow grade, 30% glass filled Flame retardant, High CTI, heat stabilized with mold release. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP LX97024 PEEK (Europe-Africa-Middle East) LNP* LUBRICOMP* LX97024 is a compound based on Polyetheretherketone containing Glass Fiber, PTFE. Added features include: Internally Lubricated, Easy Molding. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | ASTM D790 |
Toyobo Vylopet® EMC130-04 Glass Reinforced Polyester, Easy Molding Grade Key Feature: Flame retardant V-0 UL-94 classApplications: General componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and tracking r.. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | ASTM D790 |
Toyobo Vylopet® EMC430 PET/PBT Blend Key Feature: HB UL-94 ClassApplications: general and high rigidity componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, good mechanical pro.. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | ASTM D790 |
Solvay Specialty Polymers Amodel® AF-1550 V0 Polyphthalamide (PPA) Resin, 50% Glass/Mineral Reinforced, at 50% RH
& Data provided by the manufacturer, Amoco Corporation.AMODEL AF-1550 V0 resin is a 50% glass/mineral reinforced, flame retarded polyphthalamide (PPA) that features: high deflection temperature, high .. |