Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 162 MPa | 23500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL146 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL146 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Flexural Yield Strength | 162 - 241 MPa | 23500 - 35000 psi | Average value: 195 MPa Grade Count:5 |
Overview of materials for Nylon 12, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. .. |
|||
Flexural Yield Strength | 162 MPa @Thickness 3.20 mm |
23500 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMAX GP5306F PBT+ABS+GF30%, Flame Retardant Description: Injection Molding Grade, PBT+ABS+GF30%, Flame RetardantApplication: E&E (Connector)CAS: 9003-56-9, 68928-70-1, 65997-17-3, 24968-12-5, 9003-54-7 and 1309-64-4Information provided by LG .. |
|||
Flexural Yield Strength | 162 MPa @Thickness 3.20 mm |
23500 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP2130AE PA6+GF13%, General Purpose Feature: Injection Molding, PA6+GF13%, General PurposeApplication: Industrial MaterialCAS No. 25038-54-4 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 162 MPa | 23500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Stat-kon AE004E ABS LNP* Stat-Kon* AE004E is an ABS compound containing Glass Fiber. Characteristics of this grade are Statically Conductive and Easy Molding.This data was supplied by SABIC-IP for the Americas region... |
|||
Flexural Yield Strength | 162 MPa | 23500 psi | ASTM D790 |
Techmer ES Plastiblend® PBT/ABS GF/M40 FR 40/40% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral Fiber Reinforcement, 40/40% Filler by WeightFeatures: Flame RetardantInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 162 MPa | 23500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP LF002 PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LF002 is a compound based on Polyetheretherketone resin contaninig Glass Fiber. |
|||
Flexural Yield Strength | 162 MPa | 23500 psi | ASTM D790 |
Samyang Tramid® 210G15 Polyamide, Reinforced Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.210G15 is a reinforced grade.Applications:Automotive gear level housingConnectors.. |
|||
Flexural Yield Strength | 162 MPa | 23500 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GFN3 PPE+PS PPE+PS blend. 30% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Sui.. |
|||
Flexural Yield Strength | 162 MPa | 23500 psi | ASTM D790 |
Cheng Yu Plastic FV30725 POM, 25% Mineral Reinforced |
|||
Flexural Yield Strength | 162 MPa | 23500 psi | ASTM D790 |
Cheng Yu Plastic FV30G15 POM, 15% Glass Fiber |
|||
Flexural Yield Strength | 162 MPa | 23500 psi | ASTM D790 |
PolyOne Lubri-Tech™ ES-20GF/15T Polyethersulfone - 20% Glass Fiber Reinforced - 15% PTFE Lubricated
(disconti Data provided by PolyOne. |
|||
Flexural Yield Strength | 162 MPa | 23500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP VERTON MV006BS PP LNP* VERTON* MV006BS is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this grade include: Heat Stabilized, Burst Pressure, Structural, Chemically Coupl.. |