Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 138 - 186 MPa | 20000 - 27000 psi | Average value: 165 MPa Grade Count:8 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 30% Carbon Fiber Filled". Specific grades with carbon fiber conte.. |
|||
Flexural Yield Strength | 138 - 348 MPa | 20000 - 50500 psi | Average value: 251 MPa Grade Count:34 |
Overview of materials for Nylon 612, Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Carbon Fiber Filler". Each property range of values reported is minimum and maximum values of.. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFL22E PA6.6 (Europe-Africa-Middle East) LNP* LUBRICOMP* RFL22E Is a compound based on PA66 resin, containing Glass Fiber and PTFE. Added features include: Internally Lubricated, Easy Moulding |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Techmer ES Electrablend® ABS CF30 BK 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Europe-Africa-Middle East) High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM UF5011S PEI (Asia Pacific) Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF002 PC LNP THERMOCOMP* DF002 is a compound based on Polycarbonate resin containing 10% Glass Fiber. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Techmer ES Plastiblend® PA6/6 M L Nylon 66 Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: Fast Molding Cycle, Low Viscosity and LubricatedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Sumitomo Bakelite North America 2004B Glass Reinforced Hardware Grade Epoxy Epoxy is the premier material for military firewall connectors.Information provided by Sumitomo Bak North America, Inc. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Asia Pacific) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
PlastxWorld CEVIAN® A2606 30% GF PA/ABS Alloy, Conditioned Property data is for samples at equilibrium moisture (0.7%)These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWo.. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Clariant Renol BR2029 Nylon 66, General Purpose, Black Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Clariant Renol PA101L Nylon 66, General Purpose, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Clariant Renol PA113 Nylon 66, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 137.9 MPa | 20000 psi | |
Abatron AboCast/AboCure 8109-1 High melting point.Processing: 100/30 pbw; mix at 130-140°C (270 °F); cures in 16 h/120°C (250°F), 10 h/140°C (285°F), 8 h/160°C (320°F), 2 h/ 200°C (390°F).Applications: Heavy duty castin.. |
|||
Flexural Yield Strength | 137.9 MPa | 20000 psi | |
Abatron AboCast/AboCure 8109-11 All-purpose, structural dielectric resin. Better thermal and chemical properties than 8109-8, but requires heat cure. Melts at 70-80°C and remains liquid (supercooled) for many hours at RT.Process.. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | |
Bulk Molding Compounds BMC 845 Vinyl Ester Molding Compounds, 30% Glass-Filled Description: BMC 845 is designed for use in PEM type fuel cell applications such as end plates and manifolds. It is a corrosion resistant product that shows outstanding creep resistance and compress.. |
|||
Flexural Yield Strength | 138 - 216 MPa | 20000 - 31300 psi | Average value: 190 MPa Grade Count:34 |
Overview of materials for Polycarbonate, 40% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 40% Glass Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Flexural Yield Strength | 138 - 193 MPa | 20000 - 28000 psi | Average value: 175 MPa Grade Count:22 |
Overview of materials for Polyethersulfone (PES), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 20% Glass Fiber Filled". Each property range of values reported is minimum and m.. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
PolyOne Lubri-Tech™ MP-30GF/15T Modified PPO - 30% Glass Fiber - 15% PTFE
(discontinued **) Data provided by PolyOne. |
|||
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Techmer ES HiFill FR® PA6/6 GF10 FR BK 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightFeatures: Flame Retardant Appearance: BlackProcessing Method: Injection MoldingInformation provided by.. |
|||
Flexural Yield Strength | 137.9 MPa | 20000 psi | |
Abatron AboCast/AboCure 8109-7 Processing: 100/80 pbw; Potlife: 6-7 days/20°C (68°F), 12-24 h/40°C (105°F), 0.75-7 h /60°C (140°F); mix at 50-80°C (120-175°F); cures in: 1 h/100°C (212°F) + 4 h/150°C (300°F) postcure... |