Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 130 MPa | 18900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Opnyl OP66GF13 Nylon 66, 13% Glass Reinforced Nylon 66 - Glass reinforced (13 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Uttap SF 600 Polyethersulfone Polyether Sulfone Resin-Medium Viscosity, unreinforced standard grade for Easy Injection Molding.Information provided by Ovation Polymers |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP COLORCOMP J1000Z PES (Europe-Africa-Middle East) LNP* COLORCOMP* is a compound based on Polyethersulfone resin. Added features include: High Viscosity |
|||
Flexural Yield Strength | 130 MPa @Temperature 90.0 °C |
18900 psi @Temperature 194 °F |
ISO 178, ASTM D790 |
Nilit Nilamid A G5 FR C4 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Halogens) Description: Nilamid A G5 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This produ.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | ISO 178, ASTM D790 |
Nilit Nilamid B G4 FR HF 20% Glass Fiber Reinforced, Flame Retardant PA6 Description: Nilamid B G4 FR HF is a NYLON 6 based flame retardant compound that does not contain any halogen or red phosphorous. It has a good overall mechanical performance, has an excellent price.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | DIN 53 452 |
Albis Plastics Tedur® L 9561 PPS, 60% Glass Fiber/Mineral
(discontinued **) High Gloss, Highest Surface Finish, Metallization w/o Base Coating. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Various High Temperature ReflectorsProcessing: Inje.. |
|||
Flexural Yield Strength | 130 - 388.175 MPa @Temperature -40.0 - 121 °C |
18900 - 56300.1 psi @Temperature -40.0 - 250 °F |
Average value: 225 MPa Grade Count:8 |
Overview of materials for Nylon 66, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. .. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | ASTM Data |
BASF Capron® 1202CQ Nylon 6 (Dry)
(discontinued **) Capron 1202CQ is a blended low viscosity, polyamide 6 injection molding homopolymer, possessing a modified crystalline structure for increased property performance and faster cycles. It is also ava.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | ASTM Data |
BASF Capron® 5202 HS Blend Nylon 66 (Dry)
(discontinued **) Capron 5202 HS Blend is a blended, unfilled, heat stabilized, nylon 6,6, injection molding compound. It is also available in natural and pigmented versions. It combines strength and stiffness as wel.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | ASTM D790 |
Lucky CF-920 Acrylic May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and coloring capability. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | ASTM D790 |
Lucky EG-920 Acrylic, Extrusion Grade Special extrusion grade with excellent stress cracking resistance, intended mainly for exterior applications. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, hi.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | ASTM D790 |
Lucky EG-930 Acrylic, Injection Grade Injection molding grade. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and coloring capability.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP UAL23AS PPA (Europe-Africa-Middle East) LNP* LUBRICOMP* UAL23AS is a compound based on Polyphthalamide resin containing Aramide Fiber, PTFE. Added features include : Internally Lubricated, Heat Stabilized. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM 4002 PEI PTFE filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL 94 V0 and 5VA listing in recognized colors. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM 9075 PEI (Europe-Africa-Middle East) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM LTX300A PEI Copolymer High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem LTX300A PEI Copolymer (Europe-Africa-Middle East) High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 4012 PBT (Europe-Africa-Middle East) VALOX 4012 is a 10% high strength glass fibre reinforced PBT injection moulding resin with improved mechanical properties. Applications: connectors. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® DR48 PBT (Europe-Africa-Middle East) VALOX DR48 is a 17% glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromoto.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® ENH4530 PBT (Europe-Africa-Middle East) 15% GF PBT, Non-Brominated & Non-Chlorinated Flame retardant |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP WFB62 PBT LNP* THERMOCOMP* WFB62 is a compound based on PBT resin containing 10% Glass Fiber, 10% Glass Bead. Added feature of this grade is: Low Warpage. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PKN4752 PPE+PS (Europe-Africa-Middle East) NORYL PKN4752 is a translucent, high heat PPO+PS extrusion grade for dilution with polystyrene resin. It is suitable for (microwavable) food packaging and is compliant with US and European food cont.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM LTX300A PEI Copolymer (Asia Pacific) High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | ISO 178 |
Wellman Wellamid® MR410 42H-N 40% Mineral Reinforced Nylon 6, Heat Stabilized Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | ISO 178-93 |
Wellman Wellpet® MRGF101-GY1 PET, 29% Mineral/Glass Fiber Reinforced Typical data obtained from injection molded test bars, tested dry as molded at 73°F (23°C). Information provided by Wellman, Inc. Engineering Resins Division. |
|||
Flexural Yield Strength | 130 - 150 MPa | 18900 - 21800 psi | ASTM D790 |
Chang Chun Plastic PBT3015 15% Glass Fiber Enforced PBT Information provided by Dowell Trading Company Ltd. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | ASTM Data |
BASF Capron® 8360 HS 34% Mineral-Filled Nylon 6 (Dry)
(discontinued **) Capron 8360 HS is a heat stabilized 34% mineral reinforced nylon 6 injection molding resin possessing a high level of toughness and ductility combined with excellent processability and surface aesth.. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | ASTM D790 |
E-Polymers Tekaloy® T80G20 , 20% Glass Fiber Reinforced PBT/ABS Alloy 20% Glass Fiber reinforcedInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Yield Strength | 130 MPa | 18900 psi | ASTM D790 |
Chevron Phillips Ryton® PR09-60 Polyphenylene Sulfide Compound, Annealed 2 hours at 200°C
(discontinued **)&l Polyphenylene Sulfide CompoundRyton® PR09-60 Annealed 2 hours at 200°C is pelletized unfilled high molecular weight polyphenylene sulfide resin suitable for extrusion or injection molding.Comments.. |
|||
Flexural Yield Strength | 130 - 265 MPa | 18900 - 38400 psi | Average value: 182 MPa Grade Count:42 |
Overview of materials for Polyethylene Terephthalate (PET), Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Glass/Mineral Reinforced". Each property range of values reported is m.. |