Polymer Property : Flexural Yield Strength = 14800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	102 MPa	14800 psi	ASTM D790
Nylene® 451 Nylon 6 Dry as molded. Injection molding grade. Nylene 451 is recommended for molding applications requiring both maximum durability and toughness. Exceptional fatigue and wear resistance insure long produ..
Flexural Yield Strength	102 MPa	14800 psi	ASTM D790
Nylene® 454 Nylon 6 Dry as molded. Injection molding grade. Nylene 454 is the heat stabilized version of 451 recommended for molding applications requiring both maximum durability and toughness. Exceptional fatigue an..
Flexural Yield Strength	102 MPa	14800 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® C2950 PC+ABS Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced flow and impact plus improved heat resistance intended for various applications.
Flexural Yield Strength	102 MPa	14800 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® C2950 PC+ABS (Asia Pacific) Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced flow and impact plus improved heat resistance intended for various applications.
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® CY6120 PC+ABS Non-chlorinated and non-brominated flame retardant PC/ABS featuring good flow and impact properties. UL-94 V0 listed at 1.2mm intended for various thin wall applications.
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 9945A PC Lexan* resin 9945A Polycarbonate (PC)is a non-filled, injection moldable grade. This non-chlorinated, non-brominated PC has an UL-94 V0 rating at 1.8 mm. Lexan resin 9945A is available in clear tr..
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® BPL1000 PC Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U..
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® BPL1000 PC (Asia Pacific) Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U..
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® BPL1000 PC (Europe-Africa-Middle East) Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U..
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® FST9436 PC Copolymer Medium viscosity opaque, low smoke, and OSU 65/65 compliant PC Copolymer
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Lexan® FXD9945A PC UV stabilzed Visualfx FR PC with non-brominated and non-chlorinated flame retardant systems. It is available Only in white diffused effect(WH8B111X) meeting UL-94 V0 at 2mm for thin wall application..
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD4211 PC (Asia Pacific) Lexan* HFD4211 is a 10% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HP1HF PC (Europe-Africa-Middle East) Very high flow, biocompatible polycarbonate for healthcare applications. EtO sterilizable.
Flexural Yield Strength	102 MPa	14800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP FARADEX DX11003 PC (Europe-Africa-Middle East) LNP FARADEX DX11003 is a compound based on Polycarbonate resin potentially suitable to meet high frequency electromagnetic absorption requirments. The compound is also an excellent candidate for man..
Flexural Yield Strength	102 MPa	14800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP FARADEX NS0031 PC+ABS (Asia Pacific) Faradex NS0031 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel. Added features of this material include: EMI/RFI Shiel..
Flexural Yield Strength	102 MPa	14800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFP34 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFP34 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Silicone.
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® HFD4211 PC (Europe-Africa-Middle East) Lexan* HFD4211 is a 10% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Flexural Yield Strength	102 MPa	14800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP BG004 SAN (Europe-Africa-Middle East) LNP* LUBRICOMP* BG004 is a compound based on Styrene Acrylonitril resin containing Graphite. Added features include: Internally Lubricated.
Flexural Yield Strength	102 MPa	14800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RX05487 PA 66 LNP* LUBRICOMP* RX05487 is a compound based on Nylon 66 containing 10% Aramid Fiber, 10% Lubricant. Added features of this material are: Low Warpage, Wear Resistant.
Flexural Yield Strength	102 MPa	14800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON DD0009XP PC (Asia Pacific) LNP* Stat-kon* DD0009XP is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include:Electrically Conductive, Flame Retardant. Also known as Stat-Kon*..
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP ZX06323 PPE+HIPS (Asia Pacific) This material is mineral filled PPO grade with high dielectric constant and low loss tangent
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL NH7010 PPE+PS Noryl* NH7010 resin is a modified PPE-PS blend that exhibits an excellent balance of non-halogenated flame retardance, high heat resistance, good flow, and low specifc gravity for light weight parts..
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL NH7010 PPE+PS (Asia Pacific) High heat, Non halogenated flame retardant Noryl product
Flexural Yield Strength	102 MPa	14800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp MF004S PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MF004S is a compound based on Polypropylene resin, containing Glass Fiber. Added features include; Chemically Coupled.This data was supplied by SABIC-IP for the Europe-Africa-Middle..
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP NF001 PC+ABS LNP THERMOCOMP* NF001 is a compound based on PC+ABS resin containing 5% Glass Fiber.
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP NF001XXX PC+ABS LNP* THERMOCOMP* PCA-F-1001 is a compound based on PC+ABS resin containing 5% Glass Fiber.
Flexural Yield Strength	102 MPa	14800 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL EN7010 PPE+SEBS (Asia Pacific) High heat, Non halogenated flame retardant Noryl product for Film
Flexural Yield Strength	102 MPa	14800 psi	2 mm/min; ISO 178
Eurostar Starpylen MF004S PP, 20% Glass Fiber Filled, Injection Molded Starpylen MF004S is a 20% Glass Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
Flexural Yield Strength	102 MPa	14800 psi
Phenolic 46%, Carbon fabric 54% Phenolic - Monsanto "SC 1008". Carbon fabric - "VCA"
Flexural Yield Strength	102 MPa	14800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL FE8000S PPE+PS (Asia Pacific) Noryl* FE8000S resin is an unfilled modified polyphenylene ether resin designed for fluid handling applications. This resin is suitable for multiple conversion routes and will be available in custom..