Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® C1204HF PC+ABS (Europe-Africa-Middle East) High heat PC/ABS blend offering good flow and excellent impact. Food compliant according to FDA and European directive 2002/72/EC. Available in limited colors. Effective January 15th, 2008 this gra.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CU1650 PC+ABS (Asia Pacific) UV stabilized, non-FR PC/ABS of excellent flow and impact performance |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CU1650 PC+ABS (Europe-Africa-Middle East) UV stabilized, non-FR PC/ABS of excellent flow and impact performanceThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS (Europe-Africa-Middle East) CYCOLOY CX1440 is a general purpose PC+ABS blend specially developped for thin wall applications requiring weld line strength and high flow with a good balance of propertiesThis data was supplied by.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS (Europe-Africa-Middle East) CYCOLOY CX1440 is a general purpose PC+ABS blend specially developped for thin wall applications requiring weld line strength and high flow with a good balance of propertiesThis data was supplied by.. |
|||
Flexural Yield Strength | 80.0 MPa @Temperature 90.0 °C |
11600 psi @Temperature 194 °F |
ISO 178, ASTM D790 |
Nilit Nilitop BT G4 FR C3 is a 20% Glass Fiber Reinforced, Flame Retardant PBT Description: Nilitop BT G4 FR C3 is a 20% glass fiber reinforced, flame retardant PBT with halogens. The flame retardant does not contain PBB and PBDE, so it is compliant with the WEEE directive. It.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CY8540 PC+ABS (Europe-Africa-Middle East) CYCOLOY CY8540 is a PC+ABS blend, especially designed for textile backmolding in automotive interior applications. High flow grade, which allows low temperature processing to maintain fabric integri.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® EXL1036 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1036 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good h.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® FL3000 PC (Europe-Africa-Middle East) FL3000 is an FR product with excellent low temperature impact, bromine and chlorine free, good retention of properties upon weathering.This data was supplied by SABIC-IP for the Europe-Africa-Middle.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Lexan® ML7652 PC Copolymer Opaque PC-Siloxane copolymer with excellent processability. Medium flow, excellent low temperature ductility.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® XHT3141 PC Copolymer (Asia Pacific) XHT3141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® XHT3143 PC Copolymer (Europe-Africa-Middle East) XHT3143 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. It is available in a range of opaque and limited transparent colors. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP FARADEX DS0036I PC (Europe-Africa-Middle East) LNP* Faradex* DS0036I is a compound based on Polycarbonate resin containing Flame Retardant, Stainless Steel Fiber. Added features of this material include: High Impact, Flame Retardant, Non-Bromin.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP KONDUIT PX09322 PA 6 (Asia Pacific) White colored thermally conductive mineral filled PA6 FR compound |
|||
Flexural Yield Strength | 80.0 - 270 MPa | 11600 - 39200 psi | Average value: 186 MPa Grade Count:236 |
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | ISO 178, ASTM D790 |
Nilit Nilamid A3 H ZB High Impact PA66 Description: Nilamid A3 H ZB is high impact NYLON 66. The product maintains excellent impact properties, even at minus temperatures, whilst maintaining mechanical characteristics. Application areas .. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | ASTM D790 |
Asahi Kasei Tenac® LA531 Acetal Homopolymer, High Lubricity
(discontinued **) High-lubricity block copolymer with excellent friction and wear characteristics, especially on POM.Applications: Gears, keyboard parts.This product is not a part of the standard product line dated 2.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL RN0401 PPE+PS Noryl RN0401 resin is an unfilled Post Consumer Recycle (PCR) based injection moldable modified polyphenylene ether blend comprising at least 20% PCR content. Available in black only. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Europe-Africa-Middle East) Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA NORYL GTX914 is an unfilled GTX grade with an ideal combination of impact performance, dimensional stability at elevated temperatures, chemical resistance and processability. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA (Asia Pacific) NORYL GTX914 is an unfilled GTX grade with an ideal combination of impact performance, dimensional stability at elevated temperatures, chemical resistance and processability. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX GTX974 PPE+PA NORYL GTX974 is a material especially designed for in- or on-line painted bodypanels and fenders in particular. This material combines impact performance with conductivity for electro-static paintin.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® V3900WX PBT+PC (Asia Pacific) PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp MF0044E PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MF0044E is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features include: Non-Halogen Flame Retardant, Easy Molding.This data was supplied .. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | ASTM D790 |
Chase Plastics CP Pryme® A100HF ABS Features: High FlowGeneral PurposeGood toughnessForm: PelletsInformation provided by Chase Plastics. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
Eurostar Staramide BST42 PA6, Impact Modified, Injection Molded BST42 is a Low Temperature Impact Modified Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL FP5140HF PPE+PS Noryl*FP5140HF is an unfilled, injection moldable modified polyphenylene ether resin with an ISO306 Vicat B/120 of 100 deg C. Designed for good dimensional stability and high flow, this resin also u.. |
|||
Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL PX1005X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. UL746C F1. Excelent dielectric strength. Suitable for E/E market in indoor/outdoor applications. |
|||
Flexural Yield Strength | 80.0 - 227 MPa @Temperature 100 - 175 °C |
11600 - 32900 psi @Temperature 212 - 347 °F |
Average value: 129 MPa Grade Count:8 |
Overview of materials for Polyphthalamide (PPA), 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are.. |