Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 78.5 - 94.0 MPa | 11400 - 13600 psi | Average value: 82.1 MPa Grade Count:6 |
Overview of materials for Polybutylene Terephthalate (PBT), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Extrusion Grade". Each property range of values reported is minimum an.. |
|||
Flexural Yield Strength | 78.5 MPa | 11400 psi | ASTM D790 |
Samyang Triloy® 410 PC/PET alloy
(discontinued **) Characteristics:Impact resistantHeat resistantDimensional stabilityProcessabilityGood flowApplications:O/A partRear view mirror housingRice cooker baseAll information provided by Samyang |
|||
Flexural Yield Strength | 78.5 - 178 MPa | 11400 - 25800 psi | Average value: 139 MPa Grade Count:3 |
Overview of materials for PCT, 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT, 40% Glass Reinforced". Specific grades with glass content between 35% and 44% are included. Each pr.. |
|||
Flexural Yield Strength | 78.6 MPa | 11400 psi | |
Abatron AboCast 8-18/Abocure 8-18 Epoxy
(discontinued **) 2-part, clear, solvent-free dielectric epoxy casting compound.Processing: 100/32.00 ratio (pbw); Gel time, 100 g (3.5 oz.): 120 minutes; cures in 2 weeks at 25°C (77°F).Applications: solventless c.. |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical ER460 ABS, Medium Heat Resistance, High Flowability Feature: Injection Molding, Medium Heat Resistance, High FlowabilityApplication: Automobile, Motor Cycle, Electric & Electronic GoodsCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical HI121H ABS, High Stiffness Feature: Injection Molding, High StiffnessApplication: Electric & Electronic Products, Miscellaneous GoodsCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical LI911 ASA Description: Good Weatherability, High FlowApplication: Air-conditioner grill, Sawing Machine Cover, Electric/Electronic ApplicationsCAS: 26299-47-8Information provided by LG Chemical |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical LI968W Co-Extrusion ASA Description: Good WeatherabilityApplication: Window Profile, Siding, Rain GutterCAS: 26299-47-8Information provided by LG Chemical |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUCEL FW700S Modified POM, Friction Resistance, Abrasion Resistance Feature: Injection Molding, Modified POM, Friction Resistance, Abrasion ResistanceApplication: Gears, Printer Roller Pumps, Gear Worm WheelsCAS No. 66455-31-0Information provided by LG Chemical |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUCEL FW720F Modified POM, Friction Resistance, Abrasion Resistance Feature: Injection Molding, Modified POM, Friction Resistance, Abrasion ResistanceApplication: Gears, Printer Roller Pumps, Gear Worm WheelsCAS No. 66455-31-0 and 9002-84-2Information provided by LG.. |
|||
Flexural Yield Strength | 78.5 MPa | 11400 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN173HI4 High Impact Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical LUMIPLAS LD590T Light diffusion ABS Description: Extrusion, Light diffusion, High ImpactApplication: (LED) Lamp Cover, Signboard Lighting Decoration of Electronic DeviceCAS No. 9010-94-0Information provided by LG Chemical |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
LG Chemical Lupox® GP1000S PBT Description: Injection Molding, PBT, General PurposeApplication: Automotive (Connector)CAS No. 24968-12-5Information provided by LG Chemical |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY GP5006AF PC/ABS, Flame Retardant Description: Injection Molding, PC/ABS, Flame RetardantApplication: Electric and Electronic Housing and ComponentsCAS: 103598-77-2, 9003-56-9, 68928-70-1 and 1309-64-4Information provided by LG Chem.. |
|||
Flexural Yield Strength | 78.5 MPa | 11400 psi | ASTM D790 |
GRECO ISOPAK 525 ABS Resin General Purpose Injection GradeInformation provided by Greater Eastern Resins Industrial Co., Ltd. |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical SG175 ABS, Super Surface Gloss Feature: Injection Molding, Super Surface GlossApplication: Electric & Electronic ProductsCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical XR401B ABS, High Flow, Heat Resistance Feature: Injection Molding, High Flow, Heat ResistanceApplication: Automotives Exterior Housing (Side Mirror Housing, Garnish etc)CAS No. 25120-20-1, 9003-56-9, 25747-74-7 and 9003-54-7Information p.. |
|||
Flexural Yield Strength | 78.5 MPa | 11400 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN163HI High Impact Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical SG175NS ABS, Super Surface Gloss, General Anti-Static Feature: Injection Molding, Super Surface Gloss, General Anti-StaticApplication: Electric & Electronic ProductsCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical XR401 ABS, Heat Resistance Feature: Injection Molding, Heat ResistanceApplication: Electric & Electronic Housing (Frame etc) Automotives Interior & Exterior Housing (lamp housing etc)CAS No. 25120-20-1, 9003-56-9, 25747-74-7 .. |
|||
Flexural Yield Strength | 78.6 MPa | 11400 psi | ASTM D790 |
Techmer ES Electrafil® DB-1200/SS/7 ABS, 7% Stainless Steel Fiber Reinforced (dry blend) Superior cost-performance when compared with other electrically conductive resins is a hallmark of Electrafil stainless steel fiber reinforced ABS. Electrafil compounds can be formulated to meet UL.. |
|||
Flexural Yield Strength | 78.5 MPa | 11400 psi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® T102 PET, Fire Retardant Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Yield Strength | 78.5 MPa | 11400 psi | ASTM D790 |
Samyang Triloy® 225 PC/ABS alloy Characteristics:Impact resistantHeat resistantDimensional stabilityApplications:Air con. grillAll information provided by Samyang |
|||
Flexural Yield Strength | 78.5 MPa | 11400 psi | ASTM D790 |
Samyang Triloy® 230NH PC/ABS alloy, Flame Retardant Non-halogenCharacteristics:Impact resistantHeat resistantFlame retardantDimensional stabilityProcessabilityApplications:Cellular phoneMonitor housingCoffee makerHair dryerO/A partAll information pro.. |
|||
Flexural Yield Strength | 78.5 MPa | 11400 psi | ASTM D790 |
Samyang Trirex® 3000H Polycarbonate, Low-temperature Impact PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3000H is a low temperature impact grade.Applications: Mobile Phone Housing, high gloss.. |
|||
Flexural Yield Strength | 78.6 MPa | 11400 psi | ASTM D790 |
PlastxWorld CEVIAN® S3500 PC/ABS alloy Flame retarded PC/ABS Alloy.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Flexural Yield Strength | 78.6 MPa | 11400 psi | ASTM D790 |
PlastxWorld CEVIAN®-V 510 ABS High Modulus ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 6.40 mm |
11400 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IMC-45 ABS-PC Alloy ABS-polycarbonate alloys for High service temperature applications.Information provided by Bhansali |
|||
Flexural Yield Strength | 78.5 MPa | 11400 psi | ASTM D790 |
Samyang Tribit® 1800H PBT, Extruding Formality Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1800H is an extrusion grade.Information pro.. |
|||
Flexural Yield Strength | 78.5 MPa @Thickness 6.40 mm |
11400 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IMC-45 ABS-PC Alloy ABS-polycarbonate alloys for High service temperature applications.Information provided by Bhansali |