- Polymer Property : Flexural Yield Strength = 10600 psi
Polymer Property : Flexural Yield Strength = 10600 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 73.0 MPa | 10600 psi | ASTM D790 |
| Plaskolite Duraplex® 70% I Impact Modified Acrylic Sheet Continuously processed acrylic sheet.Data provided by the manufacturer, Plaskolite, Inc. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Cycolac® FR23 ABS Flame retardant ABS (non-PBBE additives). Good properties/toughness. Excellent moldability. UL94 V-0 rated. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Cycolac® MG37EPX ABS (Europe-Africa-Middle East) ABS plating grade optimized for a broad processing window for both painted and plated applications. |
|||
| Flexural Yield Strength | 73.1 MPa | 10600 psi | ASTM D790 |
| PTS Trilac® ABS-MP1000 Metal Plating Grade ABS Resin Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Flexural Yield Strength | 73.1 MPa | 10600 psi | ASTM D790 |
| PTS Trilac® ABS-HS6500 High Impact ABS Resin Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Flexural Yield Strength | 73.0 MPa @Thickness 6.40 mm |
10600 psi @Thickness 0.252 in |
2.8mm/min; ASTM D790 |
| LG Chemical LUMID HI5083A(W) PA6/ABS+MF8%, High Impact Feature: Injection Molding, PA6/ABS+MF8%, High ImpactApplication: Electric/Electronic Components (Shaver Die)CAS No. 25038-54-4, 9003-56-9, 9003-54-7 and 14807-96-6Information provided by LG Chemica.. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| LG Chemical XR-472 ABS, High Heat Resistance, High Gloss Information Provided by LG Chem |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL PX6120 PPE+PS Noryl PX6120 is an unfilled material with good flow, high Impact and chemical resistance against cleaners. Noryl PX6120 is developed for personal care appplications. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP WL0049 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WL0049 is a compound based on Polybutylene Terephalate resin containing PTFE and Flame Retardant. Added features include: Internally Lubricated, Flame Retardant. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP Lubricomp WL0049XF PBT LNP* Lubricomp* WL0049 is a compound based on Polybutylene Terephalate resin containing PTFE and Flame Retardant. Added features include: Internally Lubricated, Flame Retardant.This data was suppl.. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® 357 PBT PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures.This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® 357 PBT+PC PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® IQ357U PBT+PC Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® IQ357U PBT+PC (Asia Pacific) Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP MFB22S PP LNP* THERMOCOMP* MFB22S is a compound based on Polypropylene containing 10% Glass Fiber, 10% Glass Bead. Added feature of this grade is: Heat Stabilized. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP NX07354P PC+ABS (Asia Pacific) This is a PC/ABS compound with improved plating performance, a good candidate for Laser Direct Structuring applications. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX964W PPE+PS+PA Noryl GTX* GTX964W resin is a blend of Polyphenylene Ether and Polyamide resin with very high impact and high flow. The material wsa designed for large parts, body panels, and thinwall applications.. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® K3501 PBT Unfilled PBT, Hydrollytically Stable, Heat Stabilized, Impact Modified. A hydrollytically stable grade designed for improved performance under heat/humidity environments. Targeted at automotive unde.. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® V3900WX PBT+PC PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | ASTM D790 |
| Covestro Bayblend® 2953 Polycarbonate + ABS Blend, Automotive Plating Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
| Flexural Yield Strength | 73.0 MPa @Strain 3.50 % |
10600 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Covestro Makrolon® 1954 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Low viscosity• UV st.. |
|||
| Flexural Yield Strength | 73.0 MPa @Strain 3.50 % |
10600 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Covestro Makrolon® 2405 MAS048 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low.. |
|||
| Flexural Yield Strength | 73.0 MPa @Strain 3.50 % |
10600 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Covestro Makrolon® 2652 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Food contact quality•.. |
|||
| Flexural Yield Strength | 73.0 MPa @Strain 3.50 % |
10600 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Covestro Makrolon® 2805 MAS145 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
| Flexural Yield Strength | 73.0 MPa @Strain 3.50 % |
10600 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Covestro Makrolon® 2805 MAS152 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
| Flexural Yield Strength | 73.0 MPa @Strain 3.50 % |
10600 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Covestro Makrolon® 3152 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Food contact quality•.. |
|||
| Flexural Yield Strength | 73.0 MPa @Strain 3.50 % |
10600 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Covestro Makrolon® 3158 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc.. |
|||
| Flexural Yield Strength | 73.0 MPa @Strain 3.50 % |
10600 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Covestro Makrolon® 3258 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc.. |
|||
| Flexural Yield Strength | 73.0 MPa @Strain 3.50 % |
10600 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Covestro Makrolon® 6255 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardancy• Lo.. |
|||
| Flexural Yield Strength | 73.0 MPa | 10600 psi | chs 0.05 in/min; ASTM D790 |
| Diamond Polymers DIAMALOY 627 PC/Polyester Alloy Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||