Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 96.1 - 138 MPa | 13900 - 20000 psi | Average value: 110 MPa Grade Count:4 |
Overview of materials for PVC, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PVC, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Flexural Yield Strength | 96.1 MPa @Thickness 3.20 mm |
13900 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY GN1002FH PC, Halogen Free, Flame Retardant, Heat Resistant Description: Injection Molding, PC, Halogen Free Flame Retardant, Heat Resistant, Chemical Resistance, High ImpactApplication: IT/OA Housing and Components (Adaptor)CAS: 103598-77-2, 25232-40-0 and .. |
|||
Flexural Yield Strength | 96.1 MPa @Thickness 3.20 mm |
13900 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY GN5101RF PC/ABS Mineral Filler Description: Injection Molding, PC/ABS Mineral Filler, General Purpose, High Stiffness, Halogen Free Flame RetardantApplication: E&E (Housing), IT/OA (Notebook PC Housing)CAS: 103598-77-2, 9003-56-9.. |
|||
Flexural Yield Strength | 96.1 MPa | 13900 psi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® D201M20 PBT, 20% Mineral Filled Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Yield Strength | 96.1 MPa | 13900 psi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® D201M20 PBT, 20% Mineral Filled Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Yield Strength | 96.1 MPa | 13900 psi | ASTM D790 |
Cheng Yu Plastic B610 PC/PBT |
|||
Flexural Yield Strength | 96.1 MPa | 13900 psi | ASTM D790 |
Cheng Yu Plastic C1300 PC/ABS |
|||
Flexural Yield Strength | 96.1 MPa | 13900 psi | ASTM D790 |
Cheng Yu Plastic C6700 PC/ABS |