Polymer Property : Flexural Yield Strength = 90.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® C6600 PC+ABS (Europe-Africa-Middle East) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applicat..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® EFX810ME PC (Asia Pacific) Modified PC blend offering metallic look with minimal flowline visibility.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® 121R PC (Europe-Africa-Middle East) LEXAN 121R is a low viscosity multi purpose grade and contains a release agent to ensure easy processing. LEXAN 121R is available in transparent, translucent and opaque colours.
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® 915R PC (Europe-Africa-Middle East) Lexan* 915R Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has a UL V0 rating with good flow and mold release properties...
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® AD143 PC (Europe-Africa-Middle East) LEXAN AD143 is a medium viscosity, injection molding grade exhibiting low dust attraction. It is designed for applications with high optical requirements in terms of clarity and light transmission ..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® EXL1413T PC Copolymer (Asia Pacific) Lexan* EXL1413T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 °C) ductility in combination with medium f..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® FXD9945A PC (Asia Pacific) UV stabilzed Visualfx FR PC with non-brominated and non-chlorinated flame retardant systems. It is available Only in white diffused effect(WH8B111X) meeting UL-94 V0 at 2mm for thin wall application..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® FXE921A PC (Europe-Africa-Middle East) LEXAN FXE921A is a transparent/translucent, medium viscosity, flame retardant grade with a fluorescent appearance. Color package may affect performance.This data was supplied by SABIC-IP for the Eur..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® HP2 PC Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains m..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® HP2C PC (Asia Pacific) Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains m..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® HPX4 PC Copolymer (Asia Pacific) Medium flow specialty polycarbonate - improved processability & autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® IR 2210 PC (Europe-Africa-Middle East) PC1000 resin is a medium-low flow (MFR = 10 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold rele..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® LR180R PC (Europe-Africa-Middle East) LR180R is a medium viscosity,release containing multipurpose polycarbonate industrial gradeThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® LUX2910 PC (Asia Pacific) Global grade. LEXAN LUX2910 is an injection moulding grade especially designed for manufacturing optical parts requiring superior flow properties combined with very high transmission and color stabi..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® ML6412 PC Copolymer ML6412 is an impact modified PC resin with non-brominated, non-chlorinated flame retardant system.
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® PC0700 PC (Asia Pacific) PC0700 resin is a low flow (MFR = 7 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. It..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® PC2200R PC (Asia Pacific) PC2200R resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Flexural Yield Strength	90.0 MPa	13100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® PC2200R PC (Europe-Africa-Middle East) PC2200R resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® HP2 PC (Asia Pacific) Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains m..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® HP2NR PC Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics PC1003R PC (Asia Pacific) PC1003R resin is a medium-low flow (MFR = 10 at 300?C/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics PC1803R PC PC1803R resin is a medium-high flow (MFR = 18 at 300ÂºC/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.This data was..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics PC2200 PC (Asia Pacific) PC2200 resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release.
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics PC2203R PC (Asia Pacific) PC2203R resin is a high flow (MFR = 22 at 300?C/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Flexural Yield Strength	90.0 MPa	13100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics PC4800 PC (Europe-Africa-Middle East) PC4800 resin is a very high flow (MFR = 8.0 at 250C/1.2kg) polycarbonate product designed for use in the optical media market.
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RP002 PA 66 (Europe-Africa-Middle East) LNP* LUBRICOMP* RP002 is a compound based on PA 66 resin containing PTFE, Silicone: Added features include; Internallly Lubricated.
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX973 PPE+PA (Asia Pacific) NORYL GTX973 is a material especially designed for electrostatic painting and powder coating applications. The material combines high heat resistance with impact and conductivity in a unique way.
Flexural Yield Strength	90.0 MPa	13100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL NH4030B PPE+HIPS (Asia Pacific) NH4030B is a modified PPE-HIPS blend that presents an excellent balance of non halogenated flame retardance, lower smoke production upon burning and low specific gravity for light weight parts. Nory..
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® FXM163R PC (Europe-Africa-Middle East) PC with Visual Effect, UV-Stabilizer, Heat Stabilized, Opaque. Colour package may affect properties. Application testing always recommended.
Flexural Yield Strength	90.0 MPa	13100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Lexan® HP4EU PC (Europe-Africa-Middle East) Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mold ..