Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 52.0 MPa | 7540 psi | ASTM D790 |
Rotuba H2 Cellulose Acetate Property values at 50% RH.Data provided by the manufacturer. |
|||
Flexural Yield Strength | 52.0 MPa @Thickness 3.20 mm |
7540 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical ALPHALAC SG910 HIPS High gloss and high impact equivalent to ABS, Excellent mechanical properties compare with general HIPS, Meet requirements for cost and quality, Applications include housing of electric appliancesCA.. |
|||
Flexural Yield Strength | 52.0 MPa @Thickness 3.20 mm |
7540 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical HIPS 406AF PS, Flame Retardant Description: Injection Molding, PS, Flame RetardantApplication: Office Appliances (Parts of Printer or Copier)CAS: 9003-55-8, 25713-60-4 and 1309-64-4Information provided by LG Chemical |
|||
Flexural Yield Strength | 52.0 MPa | 7540 psi | ASTM D790 |
Hannam Chemical Hanalac 795 ABS, Pipe Grade Designed for pipe and bobbin sleeves. Excellent processability and high impact strength. Manufactured to prevent static electricity. |
|||
Flexural Yield Strength | 52.0 MPa | 7540 psi | DIN 53452; ASTM D790 |
Kolon Kopa® KN151 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Flexural Yield Strength | 52.0 MPa | 7540 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON AX01706 ABS LNP* STAT-KON* AX01706 is a compound based on ABS containing proprietary fillers. Added feature of this grade is: Electrically Conductive. |
|||
Flexural Yield Strength | 52.0 MPa | 7540 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WH0270F PBT LNP* Thermocomp* WH0270F is a dense compound based on PBT. |
|||
Flexural Yield Strength | 52.0 MPa | 7540 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY KX01002 Acetal Copolymer (Europe-Africa-Middle East) LNP* Stat-Loy* KX01002 is a compound based on Acetal Copolymer resin containing Antistat. Added features include: Permanent Anti-Static. |
|||
Flexural Yield Strength | 52.0 MPa | 7540 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp WH0270FX_WH5A289 PBT 2.7 specific gravity PBTThis data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 52.0 MPa | 7540 psi | ASTM D790 |
Eastman Tenite 360E3V45508 Propionate Water Clear, Trsp Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosi.. |
|||
Flexural Yield Strength | 52.0 MPa | 7540 psi | 6.4 mm; ASTM D790 |
SABIC Innovative Plastics NORYL FN150X PPE+PS Improved reliability and productivity. Thin wall capability. UL94 V-0/5VA rated. All data at 20% weight reduction and 0.250"" wall. |