Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 45.0 - 172 MPa | 6530 - 25000 psi | Average value: 75.2 MPa Grade Count:34 |
Overview of materials for Polybutylene Terephthalate (PBT), Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Impact Grade". Each property range of values reported is minimum and m.. |
|||
Flexural Yield Strength | 45.0 - 350 MPa @Temperature 120 - 275 °C |
6530 - 50800 psi @Temperature 248 - 527 °F |
Average value: 151 MPa Grade Count:11 |
Overview of materials for Polyetheretherketone, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Carbon Fiber Filled". Each property range of values reported is minimum and maximu.. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | DIN 53452 |
Ineos Nova S-6600 High Impact Compact Polystyrene
(discontinued **) High impact polystyrene which is very easy processed in extension and thermoforming processes. Typical applications are packaging of food stuffs like Yot beakers but technical parts and extruded pr.. |
|||
Flexural Yield Strength | 45.0 - 52.0 MPa | 6530 - 7540 psi | ASTM D790 |
Solvay Specialty Polymers Hylar® 460 PVDF Polyvinylidene Fluoride
(discontinued **) Data provided by the manufacturer.Hylar® polymers have the characteristic stability of fluoropolymers combined with a unique polarity that influences its solubility and electrical properties. In a.. |
|||
Flexural Yield Strength | 45.0 - 380 MPa | 6530 - 55100 psi | Average value: 285 MPa Grade Count:18 |
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl.. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp 4X08423 LNP* Thermocomp* 4X08423 is a compound based on Perfluoroalkoxy Polymer (PFA) containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp MX96070 PP (Europe-Africa-Middle East) LNP* STARFLAM* MX96070 is a compound based on Polypropylene resin containing Flame Retardant. Added features include: Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Middl.. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP YF003S Polyester Elastomer (Europe-Africa-Middle East) LNP* THERMOCOMP* YF003S is a compound based on Polyester Elastomer containing Glass Fiber. Added features include; Heat Stabilized. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PX1185 PPE+HIPS (Europe-Africa-Middle East) NORYL PX1185 is a special NORYL grade developed for extrusion of automotive trims. NORYL PX1185 offers high heat resistance and good impact performance. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON KD000EI Acetal Copolymer (Europe-Africa-Middle East) LNP* Stat-Kon* KD000EI is a compound based on Acetal Copolymer resin containing Carbon Powder. Added features include: Electrically Conductive, Impact Modified. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | ASTM D790 |
Tipco Tipcolene® FPC 40 - 40% Calcium Carbonate Reinforced Polypropylene Homopolymer 40% Calcium Carbonate Filled PP HomopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | ASTM D790 |
Tipco Tipcolene® FPT 20 FR VO PPC - UL94-V0 Flame Retardant, 20% Talc Polypropylene Copolymer 20% Talc Reinforced PP CopolymerApplications: Electrical & AppliancesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | 2 mm/min; ISO 178 |
Eurostar Starpylen MZ006S PP, Glass Fiber Filled, Injection Molded Starpylen MZ006S is a Glass fiber Reinforced, Polypropylene Injection Molding Resin heat stabilized (also known as Starpylen WT 30GF S3)Information provided by Eurostar. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | ASTM D790 |
Chem Polymer Durlex 709 IH PBT, Impact Modified A highly impact modified PBT exhibiting excellent toughness and processability.Data provided by the manufacturer, Chem Polymer. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | ASTM D790 |
Ineos Nova 5620 High Impact Polystyrene
(discontinued **) High heat resistance, Good balance of toughness and rigidityApplications: Food service itemProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.I.. |
|||
Flexural Yield Strength | 45.0 - 240 MPa @Temperature -40.0 - 90.0 °C |
6530 - 34800 psi @Temperature -40.0 - 194 °F |
Average value: 116 MPa Grade Count:4 |
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea.. |
|||
Flexural Yield Strength | 45.0 MPa | 6530 psi | ASTM D790 |
E-Polymers TEKAMID® TB120ST Super Tough PA6, DAM Super ToughnessInformation provided by E-Polymers Co. Ltd. |