Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 279 MPa @Thickness 3.20 mm |
40500 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP2330B(W) PA66+GF33%, General Purpose Feature: Injection Molding, PA6+GF33%, General PurposeApplication: Automotive (Air Intake Manifold, Cylinder Head Cover)CAS No. 32131-17-2 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 279 MPa @Thickness 3.20 mm |
40500 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP2330BL PA66+GF33%, General Purpose Feature: Injection Molding, PA66+GF33%, General PurposeApplication: Automotive (Radiator Tank, Reservoir)Information provided by LG Chemical |
|||
Flexural Yield Strength | 279 MPa | 40500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP UF007AS PPA (Europe-Africa-Middle East) LNP* THERMOCOMP* UF007AS is a compound based on Polyphthalamide resin containing Glass Fiber. Added features include Heat Stabilized . |
|||
Flexural Yield Strength | 279 MPa | 40500 psi | ASTM D790 |
Cheng Yu Plastic N6G45 Nylon 6, 45% Glass Filled |
|||
Flexural Yield Strength | 279 MPa | 40500 psi | ASTM D790 |
Samyang Tripet® 2500G45 Polyethylene Terephthalate, 45% Glass Fiber Reinforced TRIPET® has excellent heat resistance, good surface, chemical resistance and high electrical performance.Applications:Coil BobbinConnectorMotor HousingLamp HousingRelay BaseIron bodyAll information.. |