Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 177 MPa | 25700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36E PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DFL36E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features include; Internally Lubricated, Easy Molding. |
|||
Flexural Yield Strength | 177 - 420 MPa | 25700 - 60900 psi | Average value: 331 MPa Grade Count:45 |
Overview of materials for Polyphthalamide (PPA), 50% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 50% Glass Fiber Reinforced". Each property range of values reported is minimum and maxi.. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | ASTM D790 |
Plenco 51240 PET, Pellet, Injection Molded, Black
(discontinued **) PLENCO 51240 is an engineering grade glass reinforced flame retarded recycled polyethylene terephthalate resin designed for excellent dimensional stability. It is UL listed.Information supplied by P.. |
|||
Flexural Yield Strength | 177 MPa @Thickness 6.40 mm |
25600 psi @Thickness 0.252 in |
1.3mm/min; ASTM D790 |
LG Chemical LUCON SP9306FL sPS+MF Description Injection Molding Grade, sPS+MF, Low Thermal Conductivity, Chemical Resistance, High Heat ResistanceApplication: Electrical or Electronic Parts CAS No. 9003-53-6, 65997-17-3, 68928-70-1 .. |
|||
Flexural Yield Strength | 177 MPa | 25600 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN133G33HIBL G/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Flexural Yield Strength | 177 MPa | 25600 psi | DIN 53455; ASTM D790 |
Kolon KOPEL® KP3355 General Purpose TPE Resin KOPEL® is a thermoplastic polyester elastomer which is a new engineering rubber having combined properties of conventional rubber and thermoplastic. Its flexibility and elastic recovery are very.. |
|||
Flexural Yield Strength | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical Lupox® GP2300G PBT+GF30% Description: Injection Molding, PBT+GF30%, HCFC ResistanceApplication: E&E (Muffler of Refrigerator)CAS No. 65997-17-3 and 24968-12-5Information provided by LG Chemical |
|||
Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D570 |
LG Chemical Lupox® PBT-GP-2300 30% GFR PBT Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D570 |
LG Chemical Lupox® PBT-LW5303 30% Glass Filled Low Warp PBT Low Warpage. Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D570 |
LG Chemical Lupox® PBT-LW5303F 30% Glass Filled Low Warp Flame Retardant PBT Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
Flexural Yield Strength | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY GP2300 PC+GF30%, Heat Resistance Description: Injection Molding, PC+GF30%, General Purpose, Heat ResistanceApplication: IT/OA, E&E Housing and Components, Automotive (Interior)CAS: 103598-77-2 and 65997-17-3Information provided by .. |
|||
Flexural Yield Strength | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUPOY SC2302 PC+GF30%, High Impact Description: Injection Molding, PC+GF30%, Good Toughness, Good Impact, Chemical ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 177 MPa | 25600 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN163G30 G/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | DIN 53452; ASTM D790 |
Kolon Kopa® KN163G30 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Flexural Yield Strength | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUPOY GN2301F PC+GF30%, Halogen Free, Flame Retardant, Heat Resistance Description: Injection Molding, PC+GF30%, Halogen Free Flame Retardant, Heat ResistanceApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 65997-17-3Information prov.. |
|||
Flexural Yield Strength | 177 MPa @Thickness 3.20 mm |
25600 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUSEP SP2300 SPS+GF30%, General Purpose Feature: Injection Molding, sPS+GF30%, General PurposeApplication: Pump Units, Pick-up Lends Holder, etc.CAS No. 9003-53-6 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT LNP LUBRICOMP* WFL34H is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Healthcare. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON RFD03 PA 66 LNP* STAT-KON* RFD03 is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this material is: Electrically Conductive. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF004ER PES (Europe-Africa-Middle East) LNP* Thermocomp* JF-1004 S-3 is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® SHF4960 PBT (Europe-Africa-Middle East) Valox Super high flow grade, 30% glass filled Flame retardant, High CTI, heat stabilized with mold release. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP LX97024 PEEK (Europe-Africa-Middle East) LNP* LUBRICOMP* LX97024 is a compound based on Polyetheretherketone containing Glass Fiber, PTFE. Added features include: Internally Lubricated, Easy Molding. |
|||
Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D790 |
PlastxWorld CEVIAN® A5626 30% GF PA/ABS Alloy, DAM Property data is for dry as molded (DAM) samples.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | ASTM D790 |
Toyobo Vylopet® EMC130-04 Glass Reinforced Polyester, Easy Molding Grade Key Feature: Flame retardant V-0 UL-94 classApplications: General componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and tracking r.. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | ASTM D790 |
Toyobo Vylopet® EMC430 PET/PBT Blend Key Feature: HB UL-94 ClassApplications: general and high rigidity componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, good mechanical pro.. |
|||
Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D790 |
Cheng Yu Plastic ML3430 PC, 30% Glass Fiber |
|||
Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D790 |
Cheng Yu Plastic E2345 Flame Retardant PET, 45% Glass Fiber |
|||
Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D790 |
Cheng Yu Plastic A706G15 SAN, 15% Glass Fiber |
|||
Flexural Yield Strength | 177 MPa | 25600 psi | ASTM D790 |
Cheng Yu Plastic FV30G20 POM, 20% Glass Fiber |
|||
Flexural Yield Strength | 177 - 300 MPa | 25600 - 43500 psi | Average value: 258 MPa Grade Count:15 |
Overview of materials for Polyethylene Terephthalate (PET), 50% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 50% Glass Reinforced". Specific grades with glass content between 45% .. |
|||
Flexural Yield Strength | 177 MPa | 25700 psi | ASTM D790 |
Solvay Specialty Polymers Amodel® AF-1550 V0 Polyphthalamide (PPA) Resin, 50% Glass/Mineral Reinforced, at 50% RH
& Data provided by the manufacturer, Amoco Corporation.AMODEL AF-1550 V0 resin is a 50% glass/mineral reinforced, flame retarded polyphthalamide (PPA) that features: high deflection temperature, high .. |