Polymer Property : Flexural Yield Strength = 145 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	145 MPa	21000 psi	DIN 53 452
Albis Plastics Tedur® L V 9112-2 PPS, 20% Glass Fiber (discontinued **) Excellent Surface Finish (Additional Annealing May Be Necessary). Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Pipes, ProfilesProcessing: Extrusion (Melt Temperatur..
Flexural Yield Strength	145 MPa	21000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem 2412EPR PEI 40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Am..
Flexural Yield Strength	145 MPa	21000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem 2412EPR PEI (Europe-Africa-Middle East) 40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Eu..
Flexural Yield Strength	145 MPa	21000 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM AUT195 PEI+PCE High flow Polyetherimide blend for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 195C (SABIC test method).
Flexural Yield Strength	145 MPa	21000 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem DT1800E PEI Blend Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Americas re..
Flexural Yield Strength	145 MPa	21000 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem DT1810E PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacifi..
Flexural Yield Strength	145 MPa	21000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM DT1810EV PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed.
Flexural Yield Strength	145 MPa	21000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM EXUM0169 PEI Blend Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.
Flexural Yield Strength	145 MPa	21000 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem LTX300A PEI Copolymer (Europe-Africa-Middle East) High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East..
Flexural Yield Strength	145 MPa	21000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+HIPS (Europe-Africa-Middle East) DATA ON BK1005 ONLY.
Flexural Yield Strength	145 MPa	21000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+PS DATA ON BK1005 ONLY.
Flexural Yield Strength	145 MPa	21000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp PX05046 PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PX05046 is a compound based on PA 6 resin containing Glass Bead, Glass Fiber. Added features include: Heat Stabilized, UV-Stabilized.This data was supplied by SABIC-IP for the Europ..
Flexural Yield Strength	145 MPa	21000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP ZFM3314 PPE (Europe-Africa-Middle East) glas, mineral filled PPE
Flexural Yield Strength	145 MPa	21000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN1720 PPE+HIPS (Europe-Africa-Middle East) Noryl* GFN1720 is a 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Noryl ..
Flexural Yield Strength	145 MPa	21000 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN1720 PPE+HIPS (Asia Pacific) Noryl* GFN1720 is a 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Noryl ..
Flexural Yield Strength	145 MPa	21000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Noryl GTX GTX4110 PPE+PA66 (Asia Pacific) Non-brominated, non-chorinated Flame Retardant PPE/PA66 alloy, 10% glass reinforced. Combines ductility, modulus and high CTI with dimensional stability.This data was supplied by SABIC-IP for the A..
Flexural Yield Strength	145 MPa	21000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA (Europe-Africa-Middle East) Noryl GTX* GTX4610 resin is a high performance, 10% glass filled blend of PPE/PA that exhibits an excellent balance of non-halogenated flame retardance, dimensional stability, high heat resistance, ..
Flexural Yield Strength	145 MPa	21000 psi	ASTM D790
PlastxWorld Veroplas PA3301F Nylon 6 flame retarded (UL94 V0), 30% glass filled injection molding gradeInformation provided by PlastxWorld Inc.
Flexural Yield Strength	145 MPa	21000 psi	2 mm/min; ISO 178
Eurostar Staramide PFB42EU PA6, Glass Fiber/Bead Filled, Injection Molded Starflam PFB42EU is an UV Stabilized, Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Flexural Yield Strength	145 MPa	21000 psi	ASTM D790
Clariant Renol PCSP0009 Polycarbonate, 15% Glass Fiber, Silicone Lubricated Data provided by Clariant Masterbatches
Flexural Yield Strength	145 MPa	21000 psi	ASTM D790
E-Polymers TEKAMID® TB120G15T Impact Modified, 15% Glass Fiber Reinforced PA6, DAM 15% GF reinforced, Good impact resistanceInformation provided by E-Polymers Co. Ltd.
Flexural Yield Strength	145 MPa	21000 psi	ASTM D790
E-Polymers TEKANATE™ G720 , 20% Glass Fiber Reinforced Poly Carbonate 20% Glass Fiber reinforcedInformation provided by E-Polymers Co. Ltd.