Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 132 MPa | 19100 psi | 1.3 mm/min; ASTM D790 |
Ovation Polymers RIGITRON 10020 GF Polycarbonate, 20% Glass Reinforced PC - Glass reinforced (20 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared accor.. |
|||
Flexural Yield Strength | 132 MPa | 19100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Lubricomp DFP22H PC LNP* Lubricomp* DFP22H is a compound based on Polycarbonate containing Glass Fiber and PTFE. Characteristics of this grade are: Internally Lubricated and Healthcare.This data was supplied by SABIC.. |
|||
Flexural Yield Strength | 132 MPa | 19200 psi | DIN 53455; ASTM D790 |
Kolon SPESIN® KP213G15HI Multi Reinforced PBT Resin
(discontinued **) SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High hea.. |
|||
Flexural Yield Strength | 132 MPa | 19100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DFL12 PC LNP* Lubricomp* DFL12 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated. |
|||
Flexural Yield Strength | 132 MPa | 19200 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN3322VO Flame Retardant Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
Flexural Yield Strength | 132 MPa | 19100 psi | 50 mm/min; ASTM D790 |
LG Chemical 95HC SAN Resin Heat and chemical resistance, Good mechanical properties, Excellent processability, Superior transparency, Good dimensional stability, Applications include make-up cases and other products requiring.. |
|||
Flexural Yield Strength | 132 MPa | 19100 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY ZF3021 PPE+PS (Europe-Africa-Middle East) LNP* STAT-LOY* ZF3021 is a compound based on PPE + PS Blend resin containing Glass Fiber. Added features include Antistatic, Flame Retardant. |
|||
Flexural Yield Strength | 132 MPa | 19100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp DFZ22E PC LNP* Thermocomp* DFZ22E is a compound based on Polycarbonate with Glass and Milled Fiber. Characteristics of this products is Easy Molding.This data was supplied by SABIC-IP for the Americas region.. |
|||
Flexural Yield Strength | 132 MPa | 19200 psi | ASTM D790 |
Samyang Tribit® 1500GN15 Polybutylene Terephthalate, 15% Glass Reinforced, Flame Retardant Characteristics:G/F reinforcedFlame retardantHeat and Impact resistantApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A.. |
|||
Flexural Yield Strength | 132 MPa | 19100 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WFB33E PBT (Europe-Africa-Middle East) LNP *THERMOCOMP* WFB33E is a compound based on Polybutylene Terephalate resin containing Glass Fiber and Glass Bead. Added features include Easy Molding. |
|||
Flexural Yield Strength | 132 MPa | 19200 psi | ASTM D790 |
PlastxWorld CEVIAN® B5524 20% GF PBT/ABS Alloy Glass fiber reinforced and flame retarded PBT/ABS alloy.Information provided by PlastxWorld Inc. |
|||
Flexural Yield Strength | 132 MPa | 19100 psi | Neat Resin; ASTM D790 |
Hexcel® HexFlow® RTM 6 180°C Epoxy System for Resin Transfer Molding Monocomponent System HexFlow® RTM 6 is a monocomponent resin already degassed, specifically developed to fulfill the requirements of the aerospace and space industries in advanced resin transfer moulding (RTM) process... |
|||
Flexural Yield Strength | 132 MPa | 19200 psi | ASTM D790 |
Cheng Yu Plastic N6CV3 Flame Retardant Nylon 6, 30% Mineral Reinforced |
|||
Flexural Yield Strength | 132 MPa | 19200 psi | ASTM D790 |
Cheng Yu Plastic NG1100S Nylon 66, 10% Glass Fiber Reinforced |
|||
Flexural Yield Strength | 132 MPa | 19200 psi | ASTM D790 |
Cheng Yu Plastic FR200GV10 Flame Retardant Nylon 66, 10% Glass Fiber |
|||
Flexural Yield Strength | 132 - 269 MPa | 19100 - 39000 psi | Average value: 209 MPa Grade Count:8 |
Overview of materials for Polyethylene Terephthalate (PET), 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 40% Glass Reinforced". Specific grades with glass content between 35% .. |
|||
Flexural Yield Strength | 132 MPa | 19100 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP GFL36 PSU (Europe-Africa-Middle East) LNP* Lubricomp* GFL36 is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated. |