Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 126 MPa | 18300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP FARADEX DX92079 PC (Europe-Africa-Middle East) LNP* Faradex* DX92079 is a compound based on Polycarbonate resin containing Glass Fiber, Glass Bead, Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding, Mold Release... |
|||
Flexural Yield Strength | 126 - 317 MPa | 18300 - 46000 psi | Average value: 249 MPa Grade Count:11 |
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Flexural Yield Strength | 126 MPa | 18300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® VX5011 PBT (Europe-Africa-Middle East) VALOX VX5011 is a 10% glass fibre reinforced PBT+PC blend with low warpage characteristics. |
|||
Flexural Yield Strength | 126 MPa | 18300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL NH5020 PPE+PS Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta.. |
|||
Flexural Yield Strength | 126 MPa | 18300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL NH5020 PPE+PS (Asia Pacific) Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta.. |
|||
Flexural Yield Strength | 126 MPa | 18300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL NH5020 PPE+PS (Europe-Africa-Middle East) Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta.. |
|||
Flexural Yield Strength | 126 MPa | 18300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® SHF4930 PBT Super high flow FR PBT grade with 15% Glass reinforced |
|||
Flexural Yield Strength | 126 MPa | 18200 psi | ASTM D790 |
Cheng Yu Plastic FV30710 POM, 10% Mineral Reinforced |
|||
Flexural Yield Strength | 126 MPa | 18300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DFP32 PC LNP* LUBRICOMP* DFP32 is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
Flexural Yield Strength | 126 MPa | 18300 psi | |
Phenolic 35%, Carbon fabric 65% Phenolic - Monsanto "SC 1008". Carbon fabric - "VCA" |
|||
Flexural Yield Strength | 126 MPa | 18300 psi | DIN 53452; ASTM D790 |
Kolon Kopa® KN153G15 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Flexural Yield Strength | 126 MPa | 18300 psi | ASTM D790-70 |
Budd Hi-Flex® SMC
(discontinued **) Parts requiring high strength and dimensional stability, excellent surface smoothness without sink marks; parts to be painted requiring an automotive-type finish.Data provided by the manufacturer. |