Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 10.0 - 300 MPa @Temperature -40.0 - 250 °C |
1450 - 43500 psi @Temperature -40.0 - 482 °F |
Average value: 121 MPa Grade Count:3 |
Overview of materials for Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled". Specific grades with glass content between 45% an.. |
|||
Flexural Yield Strength | 10.0 - 300 MPa @Thickness 0.790 - 4.00 mm |
1450 - 43500 psi @Thickness 0.0311 - 0.157 in |
Average value: 121 MPa Grade Count:3 |
Overview of materials for Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled". Specific grades with glass content between 45% an.. |
|||
Flexural Yield Strength | 10.0 - 207 MPa | 1450 - 30000 psi | Average value: 52.0 MPa Grade Count:48 |
Overview of materials for Polyvinylidinefluoride (PVDF), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyvinylidinefluoride (PVDF), Molded/Extruded". Each property range of values reported is minimum and m.. |
|||
Flexural Yield Strength | 10.0 MPa | 1450 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP YP003 Polyester Elastomer (Europe-Africa-Middle East) LNP* LUBRICOMP* YP003 is a compound based on Polyester Elastomer containing PTFE, Silicone. Added features include; Internally Lubricated. |