Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 22.0 - 55.0 MPa | 3190 - 7980 psi | Average value: 41.2 MPa Grade Count:6 |
Overview of materials for Cyclo Olefin Polymer This property data is a summary of similar materials in the MatWeb database for the category "Cyclo Olefin Polymer". Each property range of values reported is minimum and maximum values of appropria.. |
|||
Film Tensile Strength at Break, TD | 35.0 - 55.0 MPa | 5080 - 7980 psi | ISO 527-3 |
Borealis Borclear™ RB707CF Polypropylene Random Copolymer for Blown Film Borclear RB707CF is a propylene-ethylene copolymer film resin without slip and antiblock additives, suitable for the manufacturing of unoriented film on blown film process.Borclear RB707CF is especi.. |
|||
Film Tensile Strength at Break, TD | 35.0 - 55.0 MPa | 5080 - 7980 psi | ISO 527-3 |
Borealis Borclear™ RD738CF Propylene Alpha Olefin Copolymer for Cast Film Borclear RD738CF is a slip and antiblock formulation propylene alpha olefin copolymer resin. It is suitable for the manufacturing of unoriented film on chill roll process.Borclear RD738CF is suitabl.. |
|||
Film Tensile Strength at Break, TD | 35.0 - 55.0 MPa | 5080 - 7980 psi | ISO 527-3 |
Borealis Borclear™ RE718CF Propylene Alpha Olefin Copolymer for Metallizable Cast Film Borclear RE718CF is a propylene alpha olefin copolymer resin formulation with antiblocking agent and without Ca-stearate, especially developed for the manufacturing of unoriented cast films for meta.. |