Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 150 ASB-X OPP Film Product Description: Bicor ASB-X is a two side coated, sealable OPP film designed for broad use in many applications, including overwrap, horizontal, and vertical packaging. This film is suitable as.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ExxonMobil Method |
ExxonMobil Bicor® 170 ASB-X OPP Film Product Description: Bicor ASB-X is a two side coated, sealable OPP film designed for broad use in many applications, including overwrap, horizontal, and vertical packaging. This film is suitable as.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 30 ARW OPP Film Product Description: Bicor ARW is a two-side acrylic coated OPP film designed for use in lamination and monoweb applications, especially for paper ream wrap. The acrylic-coated side with the higher .. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 50 LBW OPP Film Product Description: Bicor LBW is a two-sided treated, slip modified, non-heat sealable OPP film designed for use as the outside web of a lamination. The print surface is treated and can be printed .. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Metallyte® 70 MET-HB OPP Film Product Description: A vacuum-metallized, high barrier OPP film with a proprietary sealant layer. This film offers excellent moisture and oxygen barriers, hot tack, seal integrity, and lap seal rang.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Metallyte™ 18MM882 OPP Film Product Description: An ultra high barrier (UHB), biaxially oriented, multilayer polypropylene film. In addition to an excellent water vapor barrier, this film has an exceptional barrier to oxygen, .. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® A Polyester Film, 142 Gauge Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, .. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® A Polyester Film, 75 Gauge Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, .. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® D804 Polyester Film, 92 Gauge Mylar® D804 is a super clear, biaxially oriented, co-extruded polyester film, available in 60, 75 and 92 gauge. Mylar® D804 is two-side pretreated for printing and adhesive lamination. Approvals: .. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® EL Polyester Film, 92 Gauge Mylar® EL films, typically 48 through 500 gauge are strong, tough, general -purpose films for electrical/electronic uses. Heavier gauges of Mylar® EL films are similar to Mylar® MO films. Availab.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® HR951 Polyester Film, 140 Gauge Mylar® HR951 is a one-side release coated polyester film with good handling properties and clarity. It has been developed for use in various industrial applications.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® LBTW Polyester Film, 48 Gauge Mylar® LBTW is an uncoated, transparent polyester film that has been corona treated on one side to provide superior wetting and adhesion of inks, primers, and adhesives. Mylar® LBTW is commerciall.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® MDA Polyester Film, 75 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX951 Polyester Film, 105 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX951 Polyester Film, 120 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX951 Polyester Film, 140 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX951 Polyester Film, 175 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX951 Polyester Film, 48 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX951 Polyester Film, 92 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® WC Polyester Film, 92 Gauge Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® WC11/WC22 Polyester Film, 284 Gauge Mylar® type WC11 films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectric and good handlin.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Teijin® Tetoron® SLA Polyester Film, 500 Gauge Teijin® Tetoron® SLA is a super low shrinkage version of Teijin® Tetoron® type S polyester film. In addition to having the well balanced physical, chemical and electrical properties of type S fi.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ExxonMobil Method |
ExxonMobil Bicor® 210 ASB-X OPP Film Product Description: Bicor ASB-X is a two side coated, sealable OPP film designed for broad use in many applications, including overwrap, horizontal, and vertical packaging. This film is suitable as.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor™ 25 ARW OPP Film Product Description: Bicor ARW is a two-side acrylic-coated OPP film designed for use in lamination and monoweb applications, especially for paper ream wrap. The acrylic-coated side with the higher .. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® HR951 Polyester Film, 92 Gauge Mylar® HR951 is a one-side release coated polyester film with good handling properties and clarity. It has been developed for use in various industrial applications.Information provided by DuPont. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® MDA Polyester Film, 92 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® MLB Polyester Film, 48 Gauge Product Description: Mylar® MLB is an uncoated, transparent, polyester film designed for use as a component of a lamination structure and may be suitable for use in medical applications. Mylar® ML.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® WC Polyester Film, 142 Gauge Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® WC Polyester Film, 75 Gauge Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char.. |
|||
Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | ASTM D882A |
DuPont Teijin Films Mylar® WC11/WC22 Polyester Film, 142 Gauge Mylar® type WC11 films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectric and good handlin.. |